Abstract

It was predicted that the most recent technological developments in concrete technology rely on enhanced admixture efficiency rather than on improvement in cement manufacturing. Four major commercially available of organic chemical admixtures are modified lignosulfonates (LS), sulfonated naphthalene-formaldehyde resins (SNF), sulfonated melamine-formaldehyde resins(SMF) and polycarboxylate(PC). In this study, various sulfonated melamine-formaldehyde (SMF) superplasticizers were synthesized via four synthetic steps and reaction conditions such as the mole ratio of melamine to formaldehyde was changed. After application of SMF superplasticizer to cement concrete, the physical properties including workability, slump loss, compressive strength were compared with SNF

최근의 콘크리트 기술은 시멘트 제조기술의 발전 보다는 화학 혼화제의 기술발전에 의하여 성장하였다. 현재, 콘크리트 산업에 주로 사용되고 있는 4가지 화학 혼화제로서 변형된 리그닌(LS), 나프탈렌계(SNF), 멜라민계(SMF) 및 폴리카르복실레이트계(PC)계가 있다. 본 연구에서는 SMF계 고유동화제를 멜라민과 포르말린의 몰비를 변화 시키며 4단계로 나누어 반응을 진행시켰다. 합성된 SMF계 고유동화제를 시멘트 콘크리트에 적용하여 작업성, 슬럼프 손실 및 압축강도를 SNF와 비교하였다.