Abstract
The purpose of this study is to complish a method of fish glue malting with residual products such as fish head and skin discarded from sea food processing. Using the skins of Alaska pollack and file fish from fillet packers, the optimum conditions of skin glue processing were investigated and physical and chemical properties of the product were also determined. The yields of Alaska pollack, Thelagra calcogramma, skin and file fish, Novodon modestus, skin to the total body weight were $4.6\%\;and\;5.0\%$ respectively. The optimum conditions for a $49.3\%$n yield Alaska pollack skin glue processing were considered the extraction of previously tinted in $0.1\%$ calcium hydroxide solution for 3 hours with the additional water as much as 3 times of sample weight at $70^{\circ}C$ for 3 hours under the controlled pH 5.0. The conditions for file fish skin glue were similar to those of Alaska pollack except the addition of five times of water to the weight of sample skin needed for extraction. The content of crude protein of Alaska pollack and file fish skin glue were $98.0\%\;and\;96.0\%$ respectively. The contents of crude ash and crude lipid were not different from that of chemical grade gelatin. Relative viscosity, melting point, gelation temperature and jelly strength of Alaska pollack skin glue marked 5.84, $21.8^{\circ}C,\;7.1^{\circ}C\;and\;10.0g$ respectively and those of file fish skin glue showed $5.79,\;25.0^{\circ}C,\;7.4^{\circ}C\;and\;11.6g$ respectively.The color and turbidity of Alaska pollack skin glue are slightly superior to those of file fish skin glue. It is supposed that the extract residue of skin glue is valuable for use the animal feeds by the results of amino acid composition. And the ratio of each amino acid content to the total amino acid of Alaska pollack and file fish skin glue is similar to that of chemical grade gelatin.
수산물 가공시의 부산물인 어피, 어두 등을 보다 효율적으로 이용할 수 있는 방법을 검토하기 위하여 우선 어피를 원료로 피교를 가공할 때의 최적조건 및 제품의 이화열적 특성을 실험하고 아울러 제품의 구성아미노산을 분석한 결과를 요약하면 다음과 같다. 전 어체중량에 대한 피의 수율은 명태피가 $4.6\%$, 말쥐치피가 $5.0\%$였다. 명태피교 최적가공조건은 알칼리 용액 3시간, 침지용액의 알칼리농도 $0.1\%$, 첨가수량은 명태피 중량의 3배, 추출온도 $70^{\circ}C$, 추출 시간 3시간, 추출용액의 pH 5.0이었고, 말주치피교 최적 가공조건은 알칼리용액 침지시간, 침지용액의 알칼리농도, 추출농도, 추출시간 및 추출용액의 pH는 명태피교의 가공조건과 같이 첨가수량은 말쥐치피 중량의 5배였다. 일반성분 분석 결과 명태 및 말쥐치피교제품의 단백질 함량은 각각, $98.0\%,\;96\%$이었으며, 다른 일반성분 의 조성도 시판 gelatin과 비슷하였다. 명태와 말쥐치피교 제품의 점도는 5.84 및 5.79였고, 융점은 $21.8^{\circ}C$ 및 $25.0^{\circ}C$, 응고점은 $7.1^{\circ}C$ 및 $7.4^{\circ}C$이었고, jelly강도는 10.0g 및 11.6g이었다. 색도와 탁도는 명태피교 제품이 말쥐치피교 제품보다 약간 좋았다. 그리고 구성아미노산 조성으로 보아 추룰잔사도 사육원료로서 손색이 없었다. 또한 피교제품의 총아미노산에 대한 개별아미노산이 차지하는 비율은 시약급 gelatin과 거의 같았다.