Studies on Transparently Crystallized Glass -On Li2O-Al2O3-SiO2 Composition-

투명 결정화 유리에 관한 연구 -Li2O-Al2O3-SiO2계 조성에 관하여-

  • Published : 1989.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Li2O-Al2O3-SiO2 system glasses contained P2O5, TiO2 and ZrO2as the nucleating agents were melted and formed. The glass was subsequently heated first to nucleate and then to grow the crystals. At constant nucleating agent content the base glass compositions were varied and the influences of these variations on the crystallization behaviour were investigated. The study was made by measurement of thermal expansion coefficient, differential thermal analysis, X-ray diffraction analysis, scanning electron microscope observation and transmission measurement of crystallized glass specimen in visible region. It was shown that the content of crystalline phase decreased with increasing SiO2 content as well as decresing Li2O in the base glass compositions. As the result of X-ray diffrection analysis, the major crystal was $\beta$-quartz solid solution. The degree of crystallinity which was calculated using the noncrystalline scattering methods increased in S-shape with increasing heat treatment time. This change was similar to that in thermal expansion coefficient. The transmissions of 5mm thick samples were 80-90% in visible ray region.

Keywords

References

  1. British Patent 752243 S.D.Stookey
  2. Encyclopedia of Materials Science and Engineering M.B.Bever
  3. Ceramics v.21 no.5 結晶化ガラス建材 和田正道
  4. Phy.Chem.Glasses v.17 no.5 Advances in the Technology and applications of Glasses P.W.McMillan
  5. Irradiation Colours and Luminescence K.Przibram
  6. J.Mater.Sci. v.4 Transparent Glass Ceramics G.H.Beall;D.A.Duke
  7. J.Am.Ceram.Soc. v.50 no.4 Crystallization and Chemical Strength of Stuffed β-Quartz Glass-Ceramics G.H.Beall(et al.)
  8. Porcelain Enamels A.I.Andrews
  9. Introduction to Ceramics W.D.Kingery
  10. Mat.Res.Bull. v.4 S.K.Dutta;G.E.Gazza
  11. J.Am.Ceram.Soc. v.45 R.L.Cohle
  12. 作化濟夫 v.67 田代仁
  13. J.Ceram.Assoc.Japan v.76 no.9 Structural Change during the Process of Formation of a Transparent Glass-Ceramics Y.Moriya
  14. Nucleation and Crystallization in Glass v.1 TiO₂ and ZrO₂as Nucleants in a Lithia alumina Silicate Glass-Ceramics D.R.Stewart
  15. Glastech. Ber v.60 no.7 Nucleation in a Precursor Glass for a Li₂O-Al₂O₃-SiO₂ Glass-Ceramics U.Schiffner;W.Pannhorst
  16. J.Am.Ceram.Soc. v.41 no.4 Determination of Percent Crystallinity of Partly Devirified Glass by X-ray Diffraction S.M.Ohlberg;D.W.Strickler
  17. 日本特公,昭4039-21049 田代仁,;?木淸;和田正道;田中一好
  18. 日本特公,昭40-20182 ?木淸;和田正道;田中一好
  19. Glass-Ceramics P.W.McMillan
  20. X線回折에 따른 化學分析 久保;加藤編
  21. Glass Tech. v.19 no.5 Microstructure of Glass-Cermics and Photosensitive Glasses G.H.Beall
  22. J.Am.Ceram.Soc. v.57 no.7 Thermal Expansion of beta-Eucryptite H.Schulz