Abstract

The fatigue life and crack penetration behavior of high strength steel have been studied in detail both experimentally and analytically. The fatigue crack shape of a smooth specimen is almost semicircular, while a specimen with stress concentration becomes semielliptical according to stress concentration shape. The aspect ratio of smooth specimens calculated using the Newman-Raju's formular is smaller than the value obtained from the experiment. On the other hand, the aspect ratio of the stress concentration specimen shows a good agreement with experimental results. It is found that the crack growth behavior on the back surface after the penetration is unique and can be divided into three stages ; rapid growth region, constant growth region and acceleration growth region. By using the K value suggested in this study, the particular crack growth behavior and crack shape can be estimated quantitatively.

본 연구에서는 평활부 및 응력집중부에 표면균열을 갖는 표면균열재의 피로수 명과 균열관통 거동을 검토하고, 그 특성을 해명하였다.

Keywords

• Fatigue;
• LBB Desin;
• Surface Crack;
• Stress Concentration;
• Crack Growth;
• Crack Penetration

• 피로;
• 파단전누설설계;
• 표면균열;
• 응력집중;
• 균열성장;
• 균열관통;