Mechanical Properties of High Strength Cement Composite with Carbon Fiber

탄소섬유 보강 고강도 시멘트 복합체의 기게적 특성에 관한 연구

  • 전용희 (인하대학교 무기재료과) ;
  • 한기성 (인하대학교 무기재료과)
  • Published : 1993.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Two sheets of high strength cement paste using ordinary Portland cement and water soluble polymer (polyacrylamide) were made by kneading with a twin roll mill. A carbon fiber layer out between two sheet of the cement paste, and then carbon fiber reinforced high strength cement composites were prepared by pressing them. The mechanical properties of the composites were investigated through the observation of the microstructure and the application of fracture mechanics. When the carbon fiber was added with 0.2 and 0.3wt% to the composites the flexural strength and Young's modulus were about 110∼116MPa and 74∼77GPa respectively, and critical stress intensity was about 3.14MPam1/2. It can be considered that the strength improvement of high strength cement fiber composites may be due to the removal of macropores and the increase of various fracture toughness effects; grain bridging, frictional interlocking, polymer fibril bridging and fiber bridging.

Keywords

References

  1. European Palent publication no.9921685 J.D. Birchall;A.J. Howard;K. Kendall
  2. Nature v.298 Flexural Strength and Porosity of Cement J.D. Birchall.A.J. Howard;K. Kendall
  3. 한국요업학회지 v.27 no.4 고강도 시멘트 경화체의 특성에 미치는 혼합재의 영향 김정환;최상흘;한기성
  4. 한국요업학회지 v.27 no.7 고강도 시멘트의 특성에 미치는 미세구조의 영향(Ⅰ) 김정환;최상흘;한기성
  5. 한국요업학회지 v.27 no.8 고강도 시멘트의 특성에 미치는 미세구조의 영향(Ⅱ) 김정환;최상흘;한기성
  6. Proc. 9th Int. Cong. Chem. Cem. v.Ⅲ Mechanical Properties of MDF Cement Composites with SiC Powder J.H. Kim;K.S. Han;S.H. Choi
  7. セラミクスの力學的特性評價 西田俊彦;安田榮一
  8. J. Am. Concr. Inst. no.11-62 Influence of Aggregate and Voids on Modulus of Elasticity of Concrete, Cement Mortar and Cement Paste Torben C. Hansen
  9. Cem Conc. Res. v.12 Physical Properties of High Strength Cement Pastes N. McN. Alford;G.W. Groves;D.D. Double
  10. J. Am. Ceram. Soc. v.70 no.4 Crack-Interface Grain Bridging as a Fracture Resistance Mechanism in Ceramics;Ⅰ, Experimental Study an Alumina Peter L. Swanson;Carolyn J. Fairbanks;Brian R. Lawn;Yiu-Wing Mai;Bernard J. Hockey
  11. MRS v.13 Mechanism of Crack Growth Resistance in Macro-Defect-Free Cement Paste Yiu-Wing Mai;B. Barakat;B. Cotterell;M. Swain
  12. J. Mater Sci. v.19 The Mechanical Properties and Tensile Failure Mechanism of a High Strength Polymer Modified Portland Cement N.B. Eden;J.E. Bailey
  13. Composites Science and Technology v.37 Toughness, Microstructure and Interface Charateristics for Ceramic-Ceramic Composites H. Osmani;D. Rouby;G. Fantozzi;J.M. Lequertier