Abstract

The weight loss for the mixture(raw-silk/PET) was tested to investigate the effects of weight loss accelerator on the degumming and weight loss. The degumming loss of raw-silk was decreased while the weight loss polyester(PET) was increased depending on the increase of accelerator concentration. The difference of the weight loss was not significant in raw-silk but the weight loss of PET was increased with the increase of the alkali concentration. The proper degumming of raw-silk was obtained and simultaneously the weight loss of PET was high for the raw-silk/PET "A" and "B" type. The proper degumming of raw-silk was obtained but the weight loss of PET was low for the raw-silk/PET "D" and "E" type. It showed that the typical degumming curve in raw-silk part and the weight loss of PET was increased depending on the treatment time in the weight loss for the fabric composed of raw-silk and PET.

생사와 PET로 구성된 혼섬유 재료에 대해 여러가지 조건에서 알칼리 감량을 실시하여 감량율을 조사하고, 감량촉진제가 정련, 감량에 미치는 영향에 대해 검토한 결과를 요약하면 다음과 같다. 1. 감량촉진제의 농도 증가에 따라 생사의 연감율은 감소한 반면, PET의 감량율은 증가하였다. 2. 알칼리농도 증가에 따른 감량율의 경향 차이는 인정되지 않았지만, PET의 감량율은 증가되었다. 3. PET "A", "B"와 생사로 된 혼섬유의 감량에서는, 적당한 생사의 정련과 PET의 감량이 동시에 이루어질 수 있었다. 4. PET "D", "E"와 생사로 된 혼섬유의 감량에서는, 생사는 적당한 정련이 이루어질 수 있었으나 PET의 감량율은 미미하였다. 5. 생사와 PET로 된 교직물의 감량에 있어서 생사는 전형적인 연감곡선 형태를 나타냈으며 PET는 처리시간의 경과에 따라 감량율이 계속해서 증가하였다.나타냈으며 PET는 처리시간의 경과에 따라 감량율이 계속해서 증가하였다.

Keywords

• weight loss;
• weight loss accelerator;
• degumming