Weldability of HY type High Strength-Toughness Steel

HY계 고강도 고인성강의 용접성

  • ;
  • ;
  • ;
  • Ahn, S. K. ;
  • Shim, I. O.
  • Published : 1995.09.01
Download PDF
⟨ Previous Next ⟩

Abstract

Weldability of DS100 and HY type high strength-toughness steel plates, tentatively produced as domestic production, was investigated. DS100 and DS130A had nearly same hardenability in HAZ in spite of its difference in Ceq. Based upon the y-groove test results, cold cracking susceptibility of DS130 was superior to that of DS100 because of its lower hydrogen level in weld metal. Solidification cracking tested by the Trans-Varestraint test was occured in all of the weld metals, and its susceptibility was high in the row of DS100, DS130A and DS130B. However, no liquation cracking and ductility-dip cracking tested by the Longi-Varestraint test with 6.0% augmented strain were detected in base metal and reheated weld metal. Toughness in the GMA welding joint was satisfied with the relative Mill Spec, even though welded joint of DS100 had relatively low impact energy especially at the weld metal.

Keywords

References

  1. Materials for Ocean Engineering K.Masubuchi
  2. Ocean Engineering v.1 Steels for Hydrospace J.H.Gross(et al.)
  3. Welding J. v.47 no.6 The New Development of Steel Weldments J.H.Gross
  4. Naval Engineers J. v.79 no.10 The Use of Quenched and Tempered Steels for Welded Pressure Vessels S.R.Heller
  5. 日本金屬學會會報 v.14 no.3 10Ni8°C超高張力鋼の强化機構とその特性 金澤正午;森川博文
  6. Welding J. v.45 no.9 Microcracking and Delayed Cracking in Welded Quenched and Tempered Steels C.F.Meitzner;R.D.Stout
  7. Welding J. v.48 no.9 Hydrogen Cracking in High Strength Weld Metals F.Watkinson
  8. Welding J. v.43 no.4 Delayed Cracking in Steel Weldments C.G.Interrante;R.D.Stout
  9. Welding J. v.55 no.9 Hydrogen Induced Cracking in HY-80 Steel Weldments W.F.Savage;E.F.Nippes;H.Homma
  10. Welding J. v.43 no.12 Weldability of High-Toughness Alloy Plate Steel with a Minimum Yield Strength of 140ksi A.M.Rathbone;L.P.Connor;J.H.Gross
  11. Welding J. v.45 no.11 Application of the Varestraint Technique to the Study of Weldability W.F.Savage;C.D.Lundin
  12. Welding J. v.44 no.10 The Varestraint Test W.F.Savage;C.D.Lundin
  13. Trans. of JWRI v.2 no.2 Var, straint Test for Hot Crack Susceptibility of High Strength Steels H.Kihara;F.Matsuda
  14. 溶接治金學 松田福久
  15. Trans. of JWS v.2 no.2 Fundamental Investigation on Solidification Crack Susceptibility for Weld Metals with Trans-Varestraint Test T.Senda;F.Matsuda;G.Takano;K.Watanabe;T.Kobayashi;T.Matsuzaka
  16. Met. Trans. v.13A no.7 The Effect of Quenching on the Solidification Structure and Transformation Behavior of Stainless Steel Welds S.Kou;Y.Le
  17. 溶接學會論文集 v.7 no.2 液體 Sn急冷法によるオ-ステナンレス鋼の凝固過程の檢討 松田福久;中川博二;李鍾鳳
  18. 溶接學會論文集 v.7 no.2 液體 Sn急冷法によるフェライト系ステンレス鋼の凝固過程の檢討 松田福久;中川博二;李鍾鳳
  19. 溶接學會論文集 v.7 no.3 凝固モ-ドに對するレ-ザ急冷凝固處理の影響 中尾嘉邦;西本和俊;張文平
  20. IRON-Binary Phase Diagrams O.Kubaschewski
  21. British Welding Jr. v.8 no.11 Suggested Explanation of Hot Cracking in Mild and Low Alloy Steel Welds J.C.Borland
  22. British Welding Jr. v.7 A Note on the Relationship between Chemical Composition and Hot Cracking in Mild and Alloy Steels W.K.B.Marshall
  23. Trans. of JWRI v.7 no.1 Fractographic Investigation on Solidification Crack in the Varestraint Test of Fully Austenitic Stainless Steel F.Matsuda;H.Nakagawa;S.Ogata;S.Katayama
  24. 溶接學會誌 v.47 no.8 溶接金屬のフラクトグラフイ 中用博二;松田福久
  25. Trans. of JWRI v.8 no.1 Fractographic Features and Classification of Weld Solidification Cracks F.Matsuda;H.Nakagawa