Abstract
The microcapsule for thermochromism is based on the polymerization reaction between epoxy resin and amine curing agent. The preparation process of microcapsule is based on dissolving or dispersing a hydrophobic core materials[one-dye-black(OBD), bis-phenol A(BPA), cetyl alcohol] in an aqueous solution of gelatin, epoxy resin and isophorondiamine(IPDA) ; the gelatin and IPDA used as a dispersion stabilizer and an hardening agent, respectively. The structures of epoxy resin and microcapsule materials have been analyzed by FT-IR and UV/Vis spectra. The mean diameter and size distribution of microcapsule are 1.46~1.75${\mu}{\textrm}{m}$ and 1.42, respectively. The DSC thermograms of microcapsules indicated 2 kinds of endothermic peaks at 47 and 322$^{\circ}C$. This is possibly corresponding to the melting peak of core material and wall meterial. These microcapsules are applied to the fabric by printing. Complex finished fabric showed a good wear resistance on rubbing test and the print pattern to the cotton fabric showed a reversible thermochromism ; ${\mu}_{max}$ are 580 nm below 4$0^{\circ}C$ and 276.5nm above 4$0^{\circ}C$ in ethanol/water(2/8), respectively.