Abstract
The effect of oxide additive system and $Po_2$ condition on the power loss, microstructure, initial permeability, ${\mu}_i$ vs. temperature curve of Mn-Zn ferrites has been investigated. The density and permeability increased with various additive systems while the power loss decreased. It was confirmed that the oxide additives are grain boundary materials and do not change the magnetic properties of Mn-Zn ferrites such as $T_{spm}$ and $T_c$. The ${\mu}_i$ vs. T curve indicated that $T_{spm}$ moved to the higher temperature as $Po_2$ increased. It was also confirmed that the microstructure of Mn-Zn ferrites was independent of the $Po_2$ control during cooling.
Mn-Zn 페라이트의 소결에 영향을 주는 산화물 첨가제와 자기이방성 상수( $K_{1}$)값이 zero가 되는 온도, $T_{spm}$를 결정해주는 산소분압을 변화시켜가며 전력손실, 미세구조, 초기투자율, 소결밀도, 온도에 따른 초기투자율의 변화를 관찰하였다. 산화물 첨가계는 초기투자율과 소결밀도를 증가시켰으며 동시에 낮은 전력손실을 나타내었다. 이러한 첨가제들은 입계에 석출되는 것으로 $T_{spm}$과 $T_{c}$(큐리온도)와 같은 자기적 성질을 변화시키지 않았다. 온도에 따른 초기투자율 변화는 냉각시 산소분압이 증가함에 따라 $T_{spm}$이 높은 온도로 이동함이 관찰되었다. 또한 냉각시 산소분압조절 만으로는 승온과 소결시 결정된 페라이트의 치밀화가 완전히 보정되지 못함도 확인되었다.확인되었다.