Abstract

Removal of the Arsenic components from the closed mine tailings has been attempted by the alkali-leaching method. Two tailings collected from the Daduck and Yuchon mine which were already closed many years ago were leached with caustic soda solutions. The Arsenic components in the leach liquor resulted from the alkali treatment of tailings could be removed fairly well in the form of insoluble calcium-Arsenic compound by the precipitation with calcium chloride. As a result, the extraction of about 60~90% Arsenic from the tailings could be obtained depending on the leaching conditions and the influence of temperature and the slurry density on the extraction of Arsenic was also found to be very small at the NaOH concentration more than 0.5N. In addition, it seemed that a caustic soda solution over 0.5N NaOH could be used repeatedly for the leaching of tailings since the consumption of NaOH was not so great in a leaching of them. As far as the precipitation of Arsenic components was concerned, more than 99% of Arsenic could be precipitated within 10 minutes by the addition of 2wt% CaC12 in to the leach liquor.

알칼리용출법을 사용하여 폐광산 광미로부터 비소성분을 제거하기 위한 실험을 실시하였다. 대상시료는 오래전에 폐광된 폐광산인 다덕광산 및 유천광산에서 채취한 광미를 사용하였으며, 알칼리용출액으로는 가성소다 수용액을 사용하였다. 알칼리용출후 용액중의 비소 성분은 칼슘비소화합물 형태의 불용성 침전물로 전환시키는 방법으로 제거할수 있었다. 실험결과 침출조건에 따라 약 60∼90%의 비소침출율을 달성할 수 있었으며, 0.5N이상의 가성소다 농도에서는 침출율에 대한 온도 및 슬러리 농도의 영향이 매우 작은 것으로 나타났다 또한, 1회 용출시 소모되는 알칼리 양이 별로 크지 않기 때문에 0.5N이상의 가성소다 용액을 사용할 경우 용출액 재사용이 가능한 것으로 나타났다. 한편, 비소 침전실험 결과 침출액에 대하여 2wt% 염화칼슘을 첨가함으로써 침전시간 10분이내에 99%이상의 비소 침전율을 얻을 수 있었다.

Keywords

• alkali-leaching;
• Arsenic;
• causic soda;
• extraction;
• precipitation

• 알칼리용출법;
• 비소;
• 가성소다;
• 침출율;
• 비소침전율;