초록
The paste on the glass or fabrication of the PDP(Plasma Display Panel) barrier rib was selectively etched using focused A $r_{+}$ laser(λ=514 nm) and Nd:YAG(λ=532, 266 nm) laser irradiation. The depth of the etched grooves increase with increasing a laser fluence and decreasing a laser beam scan speed. Using second harmonic of Nd:YAG laser(532 nm) the etching threshold laser fluence was 6.5 mJ/c $m^2$ for the sample of PDP barrier rib. The thickness of 180 ${\mu}{\textrm}{m}$ of the sample on the glass was clearly removed without any damage on the glass substrate by fluence of 19.5J/c $m^2$beam scan speed of 20${\mu}{\textrm}{m}$ /s. In order to increase the etch rate of the barrier rib material barrier rib samples heated by a resistive heater during laser irradiation. The heated sample has many defects and becomes to be fragile. This imperfection of the structure compared to the sample without heat treatment allows the effective etching by the focused laser beam. The etch rates were 65${\mu}{\textrm}{m}$/s and 270 ${\mu}{\textrm}{m}$/s at room temperature and 20$0^{\circ}C$, respectively.y.