The Change of Crystal Structure and Physical Properties of Partially Oriented Polyester Yarn(POY) on the Draw Ratio and Heat Setting Temperature

연신비와 열고정 온도에 따른 Partially Oriented Polyester Yarn(POY)의 구조변화와 물성

  • Published : 2000.04.01

Abstract

To examine the physical properties of POY through the microstructure control, the crystal structure such as the crystallinity, the crystallite size, the orientation, the shrinkage, the tensile properties, and the thermal stress of POY(80/48, SD) were examined at different draw ratios and annealing temperatures. From the examination following conclusions were obtained : 1. The crystallinity was more effected by the heat setting temperature than by the draw ratio. The increasing rate was greatest at the heat setting temperature range of $170~190^\circ{C}$. 2. The crystallite size perpendicular to the fiber axis was more effected by the annealing temperature at lower draw ratios. On the other hand, the crystal and amorphous orientations were more effected by the heat setting at higher draw ratios. 3. The boiling shrinkage did not change significantly, but the total shrinkage showed 13% at the draw ratio 1.9 and the heat setting temperature $170^\circ{C}$. 4. The maximum thermal stress increased with increasing the draw ratio and decreasing the heat setting temperature in the temperature range of $170~210^\circ{C}$. At the draw ratio 1.9 and the heat setting temperature $170^\circ{C}$, the maximum thermal stress found was 1.1gf/d. 5. In the heat setting temperature above $170^\circ{C}$ after the drawing, the crystallinity, the crystallite size, the orientation, and the strength increased with increasing temperature, but the shrinkage and the maximum thermal stress decreased with increasing temperature.

Keywords