Anodizing of pure Al foil for AAO as a Nanowire Template

Al 양극산화에 의한 나노선재용 AAO template제조

  • Lee Kwan Hyi (Metal Processing Research Center, Korea Institute of Science and Technology) ;
  • Lee Hwa Young (Metal Processing Research Center, Korea Institute of Science and Technology) ;
  • Jeung Won Young (Metal Processing Research Center, Korea Institute of Science and Technology)
  • 이관희 (한국과학기술연구원 금속공정연구센터) ;
  • 이화영 (한국과학기술연구원 금속공정연구센터) ;
  • 정원용 (한국과학기술연구원 금속공정연구센터)
  • Published : 2001.05.01
Download PDF
⟨ Previous Next ⟩

Abstract

AAO template having nano scale pores of high aspect ratio has been prepared through anodizing of aluminum foil in sulfuric acid electrolyte. The effect of anodizing parameters on the pore size and distribution was also examined to obtain the proper AAO as a template material of nanowire. The surface of AAO template prepared was observed by SEM to examine the mean size and distribution of pores generated by the anodizing and Fe nanowires obtained by AC electroforming using AAO template were also observed with TEM to determine the length and shape of them. From the results of work, it was found that the mean size or distribution of pores was influenced significantly by the anodizing parameters such as voltage and temperature of electrolyte. Mean length and aspect ratio of Fe nanowires prepared in the work were found to be $10{\mu}m\;and\;300\;to\;1,000$, respectively.

황산 전해질에서 고순도의 알루미늄 판재를 양극산화 시켜 이방성이 큰 나노기공을 보유한 AAO를 제조하였다. 나노선재를 제조하기 위한 template재료로서 가장 적합한 AAO를 제조하기 위해 AAO의 나노기공의 크기와 분포 등에 영향을 미치는 양극산화 변수의 영향을 조사하였다. 제조된 AAO의 SEM관찰을 통해 나노기공의 직경과 분포를 확인할 수 있었고, AAO를 template로 사용하여 교류 전주법으로 제조한 Fe 나노선재를 TEM 관찰하여 나노기공의 길이와 내부 표면상태를 확인하였다. AAO를 SEM으로 확인한 결과 전해질의 온도나 양극산화 전압 등의 변수에 따라 기공의 크기와 분포의 변화가 분명하게 관찰되었으며, 제조된 나노선재는 평균 길이 $10{\mu}m,\;300\~1000$범위의 종횡비를 갖고 있음이 TEM으로 확인되었다.

Keywords