A Study on the Synthesis and the Electrochemical Properties of $LiNi_{1-y}$${Co_y}{O_2}$from $Li_2$$CO_3$, ${NiCO_3}$, and $CoCO_3$

$Li_2$$CO_3$, ${NiCO_3}$, $CoCO_3$로부터 $LiNi_{1-y}$${Co_y}{O_2}$의 합성 및 전극특성 연구

  • Rim, Ho (Division of Advaned Materials Engineering, Automobile Hi-Technology Institute, Chonbuk National University) ;
  • Kang, Seong-Gu (Electronics and Telecommucations Research Institute) ;
  • Chang, Soon-Ho (Electronics and Telecommucations Research Institute) ;
  • Song, Myoung-Youp (Division of Advaned Materials Engineering, Automobile Hi-Technology Institute, Chonbuk National University)
  • 임호 (전북대학교 신소재공학부 자동차신기술연구소) ;
  • 강성구 (한국전자통신연구원) ;
  • 장순호 (한국전자통신연구원) ;
  • 송명엽 (전북대학교 신소재공학부 자동차신기술연구소)
  • Published : 2001.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

출발 물질로서 L $i_2$C $O_3$, NiC $O_3$, CoC $O_3$를 사용하고 조성과 합성 온도를 변화시켜, 고온 고상법에 의하여 LiN $i_{1-y}$ $Co_{y}$ $O_2$(y=0.1, 0.3, 0.5)를 합성하였다. 합성과 시료들의 결정구조, 미세구조 그리고 전기화학적 특성을 조사하였다. 80$0^{\circ}C$와 8$50^{\circ}C$에서 제조한 L $i_{x}$N $i_{1-y}$ $Co_{y}$ $O_2$는, 삼방정계(space group: R3m)의 $\alpha$-NaFe $O_2$구조로 결정화되어 있는 층상 구조를 형성하였다. LiN $i_{1-y}$ $Co_{y}$ $O_2$(y=0.1, 0.3, 0.5)는 Co의 양이 증가함에 따라 a축과 c축의 크기가 감소하였는데, 이는 코발트 이온의 크기가 니켈 이온의 크기보다 작은데 기인하는 것이다. 그러나 c축과 a축의 크기의 비(c/a)가 증가하였음은 이차원적 구조가 잘 발달됨을 보여준다. 니켈에 대한 코발트의 치환량에 따른 리튬 이온의 삽입/추출 가역성은 코발트의 치환량이 증가하면서 증가하여 y=0.3인 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$에서 대체로 우수하였고 그 이상으로 y값이 증가하면 가역성이 나빠졌다. 80$0^{\circ}C$에서 합성한 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$가 가장 큰 초기 방전 용량 146 mAh/g을 나타내었으며, 싸이클링 성능도 비교적 우수하였다. 8$50^{\circ}C$에서 합성한 LiN $i_{0.9}$ $Co_{0.1}$ $O_2$와 LiN $i_{0.7}$ $Co_{0.3}$ $O_2$가 우수한 싸이클링 성능을 보였다.다. 싸이클링 성능을 보였다.다.보였다.다.

Keywords

References

  1. Kor. J. Ceram. v.5 Synthesis of LiMn₂O₄ Cathod Materials by Emulsion Drying Method and Its Electrochemical Properties Y. K. Choi;B. H. Kim
  2. J. Kor. Ceram. Soc. v.36 Wet Chemical Preparation of Li-rich LiMn₂O₄Spinel by Oxalate Precipitation B. W. Lee;S. H. Kim
  3. J. Kor. Ceram. Soc. v.38 Combustion Synthesis of LiMn₂O₄with Citric Acid and the Effect of Post-heat Treatment Y. S. Han;J. T. Son;H. G. Kim;H.T. Jung
  4. Solid State Inoics. v.69 Why Transition Metal (Di) Oxides Are the Most Attractive Materials for Batteries T. Ohzuku;A. Ueda
  5. Mat. Res. Bull. v.20 Synthesis and Structural Characterization of The Normal Spinel Li[Ni₂]O₄ M. G. S. R. Thomas;W. I. F. David;J. B. Goodenough;P. Groves
  6. J. Electrochem. Soc. v.143 no.11 Fabrication of Thin Film $LiCo_{0.5}Ni_{0.5}O_2$ Cathode for Li Rechargeable Microbattery S.J. Lee;J. K. Lee;D. W. Kim;H. K. Baik
  7. J. Electrochem. Soc. v.142 no.12 Electrochemical Science and Technology Structure and Electrochemical Properties of $Li_{1-x}(Li_yCo_{1-у})_{1+x}O_2$ Effect of Chemical Delithiation at $0^{\circ}C$ R. Alcantara;J. Morales;J. L. Tirado
  8. J. Electrochem. Soc. v.141 no.8 Solid-state Redox Reactions of LiNi½Co½O₂(R3m) for 4 Volt Secondary Lithium Cells A. Ueda;T. Ohzuku
  9. Solid State Ionics v.90 Effect of Cobalt Substitution on Cation Distribution in $LiNi_{1-y}Co_yO_2$ Electrode Meterials A. Rougier;I. Saadoune;P. Gravereau;P. Willmann;C. Delmas
  10. Solid State Ionics v.89 Effect of Cation Mixing on the Electrochemical Lithium Intercalation Reaction into Porous $Li_{1-x}Ni_{1-y}Co_yO_2$ Electrodes Y. M. Choi;S. I. Pyun;S. I. Moon
  11. Solid State Ionics v.66 Stabilization of the Layered Crystal Structure of LiNiO₂by Co-substitution E. Zhecheva;R. Stoyanova
  12. Solid State Ionics. v.53-56 Electrochemical and Physical Properties in the $Li_xNi_{1-y}Co_уO_2$ Phases C. Delmas;I. Saadoune
  13. Solid State Communications v.90 no.7 Cobalt Segregation in the $LiNi_{1-y}Co_уO_2$ Solid Solution : A Preliminary Li NMR Study M. Menetrier;A. Rougier;C. Delmas
  14. J. Power Sources. v.54 Cobalt Stabilized Layered Lithium-Nickel Oxides, Cathodes in Lithium Rechargeable Cells B. Banov;J. Bourilkov;M. Mladenov
  15. J. Power Sources. v.43-44 The Cycling Properties of the $LixNi_{1-y}Co_уO_2$ Electrode C. Delmas;I. Saadoune;A. Rougier
  16. Solid State Ionics. v.111 Influencce of the Substitution of Fe for Mn on the Electrochemical Properties of LiMn₂O₄ M. Y. Song;D. S. Ahn;S. G. Kang;S. H. Chang
  17. Solid State Ionics. v.112 On the Capacity Deterioration of Spinel Phase LiMn₂O₄with Cycling around 4V M. Y. Song;D.S. Ahn
  18. Solid State Ionics. v.112 Improvement in the Cycling Performance of LiMn₂O₄ by the Substitution of Fe for Mn M. Y. Song;D. S. Ahn
  19. J. Power Sources v.83 Capacity Fading of Spinel Phase LiMn₂O₄ with Cycling M. Y. Song;D. S. Ahn;H. R. Park