Abstract
We made magnetite which was prepared with mixed liquids of Fe$\^$2+/and Fe$\^$3+/ added to the 3N-NaOH by coprecipitation reaction. Ahead of making magnetite, we investigated variation of physical properties for changing Fe$\^$2+/ : Fe$\^$3+/. Through the variation of the process temperature, we examined physical properties of magnetite. Also, to examine possibility of magnetic fluids, from magnetite manufactured in this way, we examined the crystal structure by X-ray diffraction pattern. The saturated magnetization $\sigma$$\_$s/, value has 60.8 emu/g, when Fe$\^$2+/ to Fe$\^$3+/ ratio is 0.46 : 0.54 in the synthetic magnetite. Keeping the condition, when the synthetic temperature is kept at 80$\^{C}$ for 30 minutes, we get $\sigma$$\_$s/, value 63.51 emu/g. It shows that $\sigma$$\_$s/, value is bigger as the synthetic temperature is higher.
Fe$^{2+}$와 Fe$^{3+}$ 의 혼합 수용액에 공침 보조 용액 3N-NaOH를 첨가해 공침 반응 시켜 Magnetite를 제조하였다. Magnetite의 제조에 앞서 첨가되는 Fe$^{2+}$이온과 Fe$^{3+}$ 이온의 비를 변화시키면서 Magnetite의 자기적 특성 변화를 조사하였다. 또한 Magnetite의 제조 온도의 변화를 통해 Magnetite의 자기적 특성 변화를 살펴보았고, 이렇게 제조된 Magnetite의 자성유체로서의 가능성을 알아보기 위해 X-ray 회절을 통해 결정성을 살펴보았다. 그 결과 Magnetite분말의 합성에서 Fe$^{2+}$와 Fe$^{3+}$ 의 비가 0.46 : 0.54일 때 Magnetite의 자기적 특성값 $\sigma$$_{s}$,는 60.8 emu/g이었고, 같은 조건에서 합성 온도를 80 $^{\circ}C$로 30분간 유지 시켰을 때의 $\sigma$$_{s}$ 값은 63.51 emu/g으로 교반 온도가 높을수록 자기적 특성값이 좋아지는 것을 알 수 있었다.다.