Abstract

In this paper, three kinds of poly(acrylate-co-methylacrylate) with different number average molecular weight(Mn) were synthesized and studied for the effects on the mechanical properties and the fluidities of the cement mortar admixtured with them. The physical properties of the cement mortar are more favorably enhanced by the poly(acrylate-co-methylacrylate) of Mn,, 5,000 than that of Mn, 2,000∼3,000. And the optimum dosage was decided to ca. 0.6 % of cement weight in cement mortar. However, the dispersion abilities of the polymers in cement mortar was not kept long time. This last result could not be explained by the theory that the fluidity of the cement mortar added with the slow releasing polycarboxylates is kept by the releasing of the carboxylic group of the copolymer in alkaline solution of cement paste.

폴리카르본산계 고분자는 분산성이 양호하고 시멘트계 재료에서 분산 유지성이 뛰어나므로 최근 콘크리트용 혼화제로 크게 주목을 끌고 있다. 따라서 본 연구에서는 시멘트콘크리트용 분산제로서 수평균 분자량(Mn)이 적당한 poly(acrylate-co-methyla-crylate)를 합성하여 시멘트 모르타르의 분산성과 기계적 물성에 미치는 영향에 대하여 연구하였다. 폴리카르본산계 고분자의 수평균 분자량이 2,000~3,000 보다 5,000 정도로 비교적 큰 polycarboxylate가 시멘트계 재료의 물성을 크게 향상시키며, 최적 첨가량은 시멘트 중량의 0.6% 이다. 그러나 poly(acrylate-co-methylacrylate)계 고분자는 시멘트 모르타르 반죽에서 흐름도의 경시변화가 큰 것으로 나타났으며, 이러한 현상은 폴리카르본산계 서방성 고분자가 시멘트계 재료에 사용되었을 때, 알칼리성 분위기에서 카르복실기의 서방성에 의해서 분산성이 지속적으로 유지된다는 기존의 이론과 다르다.

Keywords

• polycarboxylates;
• dispersion ability;
• long duration of fluidity;
• physical properties;
• slow releasing polymer

• 폴리카르본산계 분산제;
• 분산성;
• 분산 유지성;
• 물성;
• 서방성 고분자;