Abstract
The shear behavior of sawtoothed artificial joints grouted with cement milk was investigated in the laboratory under constant normal stress conditions. Tests were conducted on joints with asperities having inclinations of $16.7^{\circ}\;and\;26.6^{\circ}$, compressive strengths having $150 kgf/cm^2\;and\;423 kgf/cm^2$ under a given range of normal stresses varying from 7.75 to $19.48 kgf/cm^2$ and at a fee condition of pitching, rolling and dilatancy. Results show that the effect of asperities on shear strength increase is significant up to asperity height to grout thickness (t/a) ratio of $0.3{\sim}1.0$ and increase of cohesion is the main cause of shear strength increase in cement grouted sawtoothed artificial joints.
본 연구에서는 실내시험을 통하여 일정 수직응력 조건에서의 시멘트 주입된 톱니형 인공 절리의 전단 거동 특성을 조사하였다. 톱니 경사각이 $16.7^{\circ}$와 $26.6^{\circ}$이고, 일축압축강도가 $150 kgf/cm^2$과 $423 kgf/cm^2$인 시편에 대하여 전후거동, 좌우거동, 팽창에 대해 자유 조건에서 수직응력의 범위를 $7.75kgf/cm^2$에서 $19.48kgf/cm^2$로 변화시키면서 전단시험을 실시하였다. 실험 결과로부터 전단강도증가에 있어서 거칠기의 영향은 거칠기 높이와 주입두께의 비(t/a)가 $0.3{\sim}1.0$ 범위에서 의미가 있음을 알 수 있었으며, 시멘트 주입된 톱니형 인공절리의 전단강도의 증대 원인은 주로 점착력의 증가에 기인하는 것으로 나타났다.