Abstract
To evaluate reinforced region of dike by cement grouting, we investigated both the electrical resistivity and the strength of cement grout having various water-cement ratio with curing time. These investigation results showed that the electric conductivity of grout is much higher than that of water and that the apparent resistivity of grouted region is much lower than that of unoccupied region by grout. It was founded that electrical resistivity survey might be quite effective to detect grout region in dike. As the results of electrical resistivity sounding at three dikes, apparent resistivities after grouting showed several tens to several hundreds of ohm-m which were lower than those of pre-grouting and showed stabilizing trend with curing time. From these results, we could estimate that this behavior of apparent resistivity is due to increasing strength with curing time.
누수 보강 저수지의 그라우팅 개선 구간 평가를 목적으로 물-시멘트 배합비별로 제조된 그라우트에 대하여 재령 변화에 따른 전기비저항과 압축강도 변화를 측정하였다. 동일 조건 하에서 그라우트의 농노가 증가할수록 전도도는 높아지고, 대상 매질에 그라우트가 주입되는 경우 주입 이전에 비해 비저항이 상대적으로 낮아지는 효과가 나타나므로 이를 이용한 주입 구간의 판정이 가능함을 확인하였다. 대상 매질이 서로 다른 세 지구에 대한 그라우팅 이후 전기비저항 수직탐사 결과 겉보기 비저항은 수십∼수백 ohm-m 이하로 낮아졌으며, 주입 이후 수 일이 지난 후부터는 점차 증가된 상태로 일정하게 유지되는 것으로 나타나는데, 이는 그라우트가 주입된 이후 대상 지층 내에서 굳어짐에 따른 강도 증가의 결과로 밝혀졌다.