High Permeability, High Selectivity Carbon-Silica Membranes for Gas Separation

기체분리용 고투과선택성 탄소-실리카막

  • 이영무 (한양대학교 응용화학공학부 국가지정분리막연구실) ;
  • 박호범 (한양대학교 응용화학공학부 국가지정분리막연구실)
  • Published : 2002.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

Carbon-silica ($C-SiO_2$) membranes can be easily prepared by the pyrolysis of two-phase copolymers containing an aromatic imide block and a siloxane block and remarkably high permselectivities of $He/N_2, O_2/N_2,$ and $CO_2/N_2$. The pyrolysis of the imide-siloxane block copolymers was carried out at different final temperatures, $600^{\circ}C, 800^{\circ}C,$ and $1000^{\circ}C$ under an inert atmosphere, and is the first reported case of the precursors being used for the preparation of carbon membrane. The polymeric precursors were synthesized in a wide range of siloxane content and different final morphology, and the pyrolozed membranes were tested with a high vacuum time-lag method at $25^{\circ}C$ and 76cmHg of feed pressure. In experiments with He, $CO_2, O_2 \;and \;N_2$, the membranes were found to have good $O_2/N_2$ selectivity up to 32.2 and $O_2$ permeability on the order of $10-8/cm^2(STP)cm/cm^2seccmHg.$.

이번 연구에서 효율적인 기체분리를 위한 탄소-실리카($C-SiO_2$) 분리막이 방향족 이미드 블록과 실록산 블록으로 구성된 공중합체의 비활성분위기에서의 열분해를 통해 제조되었다. 이 탄소-실리카 기체분리막은 비교적 작은 크기의 기체분리, 즉 $He/N_2, O_2/N_2$ 그리고 $Co_2/N_2$의 분리에 있어 매우 뛰어난 기체선택도를 나타내었다. 두 상을 가진 공중합체의 열분해는 600도, 800도 그리고 1000도의 최종열분해온도로서 수행되었으며, 이러한 두 상으로 이루어진 전구체는 탄소막의 제조에 처음으로 보고되었다. 이러한 전구체는 두 상의 조성 및 같은 조성에서 중합방법의 차이에 의해 형성되는 모폴로지의 변화가 최종 탄소-실리카막의 기체분리특성에 미치는 영향을 살피기 위해 제조되었다. 이러한 탄소-실리카분리막은 $2.6-3.6{\AA}$의 동력학적 반경을 가진 작은 기체분자(헬륨, 산소, 질소, 이산화탄소)들을 사용한 기체투과실험에서, 탄소-실리카 분리막은 높은 투과도와 함께 뛰어난 분자체 효과를 보였다. 게다가 탄소-실리카분리막의 기체분리특성은 사용한 고분자 전구체의 기체분리특성과 매우 유사하며, 이것은 열적으로 안정한 두상의 사용으로 전구체의 초기 모폴로지가 열처리 후에도 상당히 유지되었기 때문이다. 현재의 연구는 탄소막 전구체의 초기의 모폴로지가 최종 탄소막의 분리특성 및 미세구조에 결정적인 영향을 미침을 암시한다.

Keywords

References

  1. Membrane Technology in the Chemical Industry S.P. Nunes;K.-V. Peinemann
  2. Nature v.318 C60: Buckminsterfullerene H. W. Kroto;J. R. Heath;S. C. O'Brien;R. F. Curl;R. E. Smalley https://doi.org/10.1038/318162a0
  3. Nature v.354 Single-shell carbon nanotubes of 1-nm diameter S. Iijima;T. Ichihashi
  4. Active Carbon C.R. Bansal;J.-B. Donnet;F. Stoeckli
  5. Microporous Mater v.4 Carbongenic molecular sieves;synthesis, properties and applications H.C. Foley https://doi.org/10.1016/0927-6513(95)00014-Z
  6. Adv. Mater v.12 Characterization of supported nanoporous carbon membranes M.B. Shiflett;J.F. Pedrick;S.R. McLean;S. Subramoney;H.C. Foley https://doi.org/10.1002/(SICI)1521-4095(200001)12:1<21::AID-ADMA21>3.0.CO;2-P
  7. J. Membr. Sci. v.177 Adsorption-selective carbon membrane for gas separation A.B. Fuertes https://doi.org/10.1016/S0376-7388(00)00458-0
  8. US Patent 4,685,940 A. Soffer;J.E. Koresh;S. Saggy
  9. Carbon v.38 Carbon molecular sieve gas separation membranes based on poly (vinylidene chloride-co-vinyl chloride) T.A. Centeno;A.B. Fuertes https://doi.org/10.1016/S0008-6223(99)00214-6
  10. Science v.285 Ultrasonic deposition of high-selectivity nanoporous carbon membranes M.B. Shiflett;H.C. Foley https://doi.org/10.1126/science.285.5435.1902
  11. Chem. Lett. v.179 H. Kita;H. Maeda;K. Tanaka;K. Okamoto
  12. J. Membr. Sci. v.160 Supported carbon molecular sieve membranes based on a phenolic resin T.A. Centeno;A.B. Fuertes https://doi.org/10.1016/S0376-7388(99)00083-6
  13. J. Phys. Chem. v.B 101 Gas permeation through micropores of carbon molecular sieve membranes derived from Kapton polyimide H. Suda;K. Haraya
  14. Carbon v.32 Carbon molecular sieve gas separation membranes-Ⅰ. preparation and characterization based on polyimide precursors C.W. Jones;W.J. Koros https://doi.org/10.1016/0008-6223(94)90135-X
  15. J. Membr. Sci. v.134 Gas permeation properties and characterization of asymmetric carbon membranes prepared by pyrolyzing asymmetric polyimide hollow fiber membrane Y. Kusuki;H. Shimazaki;N. Tanihara;S. Nakanishi;T. Yoshinaga https://doi.org/10.1016/S0376-7388(97)00118-X
  16. Carbon v.35 Preparation of platinum loaded carbon fiber by using a polymer blend J. Ozaki;W. Ohizumi;N. Endo;A. Oya;S. Yoshida;T. Iizuka https://doi.org/10.1016/S0008-6223(97)82802-3
  17. Carbon v.38 Control of pore structure in carbon T. Kyotani https://doi.org/10.1016/S0008-6223(99)00142-6
  18. New Carbons M. Inagaki
  19. Chem. Mater. Novel pyrolytic carbon membranes containing silica phase;Preparation and characterization H.B. Park;I.Y. Suh;Y.M. Lee
  20. J. Eur. Ceram. Soc. v.20 Electrical conductivity measurements in polysiloxane derived Si-O-C ceramics J. Cordelair;P. Greil https://doi.org/10.1016/S0955-2219(00)00068-6
  21. J. Membr. Sci. v.177 Percolation behavior of gas permeability in rigid-flexible block copolymer membranes H.B. Park;S.Y. Ha;Y.M. Lee https://doi.org/10.1016/S0376-7388(00)00468-3
  22. Macromolecules v.32 Percolational effect of siloxane content in poly(amideimide siloxane) on the gas permeation behavior S.Y. Ha;H.B. Park;Y.M. Lee https://doi.org/10.1021/ma9817572