Abstract
Rapeseed oil is easily oxidized due to the high contents of unsaturated fatty acid such as linoleic acid and linolenic acid. For stability of rapeseed oil oxidation, a special process is required. Two kind of simple and interesterifying mixed rapeseed oil were prepared according to add 30%, 50% and 70% of coconut oil and palm oil. Sample oils were heated at 180${\pm}$5$^{\circ}C$ for 5, 10, 15, 20, 25, 30 and 35 hours. Then the physicochemical properties such as the tendency of oxidation were investigated. The initial AV and POV of interesterifying mixed rapeseed oil were higher than those of simple mixed oil. But the tendency of oxidation were similar. While oxidation rate of similar and interesterifying mixed rapeseed oils with coconut oil and palm oil were lower about than those of rapeseed oil.
유채유에 코코넛유와 팜유를 각각 30%, 50%, 70%의 비율로 단순혼합한 혼합유와 ester 교환에 의한 혼합유를 제조하였고, 180$\pm$5$^{\circ}C$에서 가열산화시키면서 산값, 과산화물값, 요오드값, 공액이중산값 및 굴절율의 변화를 측정한 결과는 다음과 같았다. 1. 코코넛유의 산값은 25시간 가열 시까지 증가하였다가 그 이후 다소 낮아진 경향을 보였다. 또한 혼합비율에 따라 커다란 차이는 없었으나, 코코넛유와 혼합인 경우 코코넛유보다 낮은 산값을 보여주었다. 2. Ester교환에 의한 혼합유의 과산화물 초기값이 단순혼합유의 초기값보다 다소 높게 나타났으나, 증가폭에 있어서는 커다란 차이가 없었다. 코코넛유와 팜유의 혼합비율에 따라서 커다란 차이를 보이지 않았으나 혼합유의 경우가 유채유보다 낮은 값을 나타냈다. 3. 코코넛유와 팜유의 혼합시에 요오드 값의 감소가 나타났으나, 혼합방법이 요오드값의 감소현상에 크게 영향을 미치지 않는 것으로 나타났다. 4. 코코넛유와 팜유의 혼합비율이 증가함에 따라 공액이중산값의 증가폭이 다소 작아지는 현상이 나타났다. 단순혼합유와 ester 교환에 의한 혼합유의 차이는 ester교환에 의한 혼합유의 초기값이 단순혼합유의 초기값보다 다소 높은 경향이었으며 35시간 가열후의 증가폭은 커다란 차이가 없는 것으로 나타났다. 5. 코코넛유와 팜유의 혼합비율이 증가됨에 따라서는 큰 차이 없이 비슷한 정도의 굴절율 증가를 나타내고 있었다. 혼합방법의 차이에 따른 굴절율은 ester 교환에 의 한 혼합유가 단순혼합유보다 초기값에서 다소 낮은 굴절율 값을 보였다. 유채유를 포화지방산의 함량이 큰 유지와 혼합하면 유채유의 산화 안정성이 향상되는 것으로 나타났으며, 혼합방법에 따라 산화 안정성에 미치는 영향이 거의 없으므로 코코넛유나 팜유 같은 유지를 유채유에 혼합하면 튀김유로의 활용이 가능할 것으로 생각된다.