Utilization of Electric Arc furnace Slag md Converter Slag after Aging for Concrete Aggregate

콘크리트용 골재로서 에이징처리한 제강슬래그외 활용

  • Published : 2002.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

Electric arc furnace and converter slag are produced by about 6 millions tons in Korea at 2000 year. But compared with blast furnace slag, those are utilized only in unvalued material like landfill and road construction. There are unstable materials, like free CaO, in electric arc furnace and converter slag at steel-manufacturing process. This might cause volume expansion in concrete, if electric arc furnace and converter slag aggregates were used in concrete. This expansion may reach to crack or collapse of concrete. It is therefore settled by standard specification for concrete that electric arc furnace and converter slag aggregates have not to use in concrete. First of all, volume stability and stabilized process should be solved in electric arc furnace and converter slag aggregate to use in concrete. In this study, 6 types of aging are evaluated for effects of stabilization to reduce the expansion of electric arc furnace and converter slag. h converter slag aggregate, these types of aging are not good for volume stability for concrete aggregate, and even if converter slag aggregate is treated with aging, concrete with it has some problems that strength is reduced with curing days. But in electric arc furnace slag aggregate treated with hotwater and steam aging, the expansion of electric arc furnace slag aggregate is reduced about two times than that of converter slag aggregate, and electric arc furnace slag aggregate concrete has good results in strength compared with control concrete using crushed stone.

우리나라에서 2000년도에 발생된 전기로 및 전로슬래그를 합하면 약 600만 톤 정도로서 주로 도로포장재료 및 매립재 등과 같은 한정된 용도로만 활용되어 왔다. 그 이유는 제강과정 중 유리석회가 슬래그화 되지 않고 불안정한 상태로 슬래그 내부에 잔존하기 때문에 콘크리트 구조물 내에서 팽창을 일으킬 가능성이 클 뿐만 아니라, 팽창이 심할 경우 구조물의 균열 내지는 붕괴까지도 야기 시킬 수 있으므로 콘크리트용 골재로 사용해서는 안 된다고 규정하고 있다. 따라서 제강슬래그를 콘크리트용 골재로 사용하기 위해서는 제강슬래그 자체의 팽창성 억제 내지는 안정화 처리가 우선 해결되어야 할 과제로 생각된다. 본 연구에서는 제강슬래그 골재의 팽창성을 저감시키기 위한 목적으로 6종류의 에이징 방법을 선정하여 안정화의 효율에 대하여 비교 검토하였다. 전로슬래그 골재의 경우, 본 연구에서 실시한 에이징 처리 방법으로서는 콘크리트용 골재로서 요구되는 팽창률을 저감시키는데 한계가 있었을 뿐만 아니라, 에이징 처리한 전로슬래그 골재 사용 콘크리트의 강도도 재령과 더불어 감소하는 문제점이 있음을 확인하였다. 그러나 전기로슬래그 골재를 온수중 및 증기중 에이징 처리할 경우, 팽창률이 전로슬래그 골재의 약 2/3 정도에 지나지 않는 효율을 나타내었으며, 이를 사용한 콘크리트의 강도도 전로슬래그 골재 사용 콘크리트와는 달리 보통콘크리트의 강도에 상응하는 비교적 좋은 결과를 나타내므로 콘크리트용 골재로서 사용 가능성을 시사하였다.

Keywords

References

  1. "철강슬래그 재활용실적(2000)," 한국철강협회, 2001.
  2. "콘크리트표준시방서," 한국콘크리트학회, 1999.
  3. "製綱슬래그를 사용한 아스팔트鋪裝 設計施工指針," 社團法人 大韓土木學會, 1985.
  4. "電氣爐슬래그를 사용한 道路鋪裝設計.施工指針," 社團法人 大韓土木學會, 1997.
  5. Montgomery, D. G. and Wang G., "Instant-Chilled Steel Slag Aggregate in Concrete-Strength Related Properties," Cement and Concrete Research, Vol. 21, 1991, pp.1083-1091. https://doi.org/10.1016/0008-8846(91)90068-S
  6. Ozkul, M. H., "Properties of Slag Aggregate Concrete," Concrete for Environment Enhancement and Protection, 1996, pp.553-558.
  7. 沼田晉一, "電氣爐酸化スラグの骨材への利用," コンクリ一ト工學, Vol. 34, No. 7, 1996, pp.99-101.
  8. 河內睦雄, 竹內崇男, 杉浦孝行, 太田福男, "コンクリ一ト用粗骨材としての電氣爐スラグ碎石の適用性について," セ技年報. Vol. 31, 1977, pp.176-180.
  9. 河內睦雄, 推名堅太郞, 太田福男, "電氣爐スラグコンクリ一トの自然崩壞性について," セ技年報, Vol.33, 1979, pp.184-188.
  10. 川村滿紀, 鳥居和之, 二町宣洋, "轉爐スラグのコンクリ一ト用骨材として適用性," セ技年報, Vol.36, 1982. pp.136-139.
  11. 國府勝郞, "資源の有效利用とコンクリ一ト一スラグ骨材を用いたコンクリ一ト," コンクリ一ト工學, Vol. 34, No. 3, 1996, pp.88-93.
  12. 坂井正美, 宮本正友, "轉爐スラグコンクリ一ト用細骨材ヘの適用性について," 日本コンクリ一ト工學年次講演會議講演論文集, 1979, pp.185-188.
  13. 內田一郞, 出光 隆, "轉爐スラグの路盤材ヘの利用について," 土木學會論文報告集, 日本土木學會, No. 282, pp.101-113, 1979.
  14. 西 勝, 河端 薰, "路盤材としての鐵鋼スラグの基礎的性質と力學的性質," 土木學會論文集, 日本土木學會, No. 414, 1990, pp.89-98.
  15. 한기현, 김형석, 변태봉, "저 팽창성 전로슬래그 노반재 개발에 관한 연구," RIST 硏究論文, 포항산업과학연구소, Vol. 13, No. 3, 1999, pp.253-257.
  16. 高山俊一, 出光隆, 會田憲義, 衫正法, "蒸氣エ一ジングレた轉爐スラグの上層路盤材としての利用に關する硏究," 土木學會論文集, 日本土木學會, Vol. 32, No. 544, 199, pp.177-186.
  17. CAJS I-01, "遊離カルシウムの定量方法," セメント協會標準試驗方法, 1975.
  18. "製鋼スラグ路盤設計施工指針," 鐵鋼スラグ協會, 製鋼スラグ共同硏究委員會, 1985.
  19. 佐佐木 稔, 新井田有文, 大槻 孝, 土屋 桂, "エ一ジングによる轉爐スラグの安定化機構," 鐵と鋼, 日本鐵鋼協會, No. 6, 1982, pp.97-104.
  20. 成田貴一, 尾上俊雄, 高田仁輔, "轉爐スラグの風化崩壞機構について," 鐵と鋼, 日本鐵鋼協會, No. 10, 1978, pp.68-77.
  21. 井上豪, "轉爐スラグ中の晶出石灰相の水和反應," 製鋼スラグの發生量低減と資源化, 日本鐵鋼協會, 1997, pp.163-172.
  22. 富房博幸, 松永久宏, 態谷正人, 田口整司, "轉爐スラグの水和膨張に及ぼする組織形態の影響," 鐵鋼スラグの發生量低減と資源化, 日本鐵鋼協會, 1997, pp.173-181.
  23. 水渡英昭, 橫幕豊一, 林田由美子, 高橋愛和, "轉盧滓中の遊離石灰の影響による風化崩壞," 鐵と鋼, 日本鐵鋼協會, No. 14, 1977, pp.50-59.
  24. 羽場健一, 岩瀨正則, "CaOの水和反應速度," 製鋼スラグの發生量低減と資源化, 日本鐵鋼協會, 1997, pp.201-205.
  25. Lerch, W. C., "Concrete Aggregate - Chemical Reactions," Significance of Test and Properties of Concrete and Concrete Aggregates, 1956.
  26. Hansen, W. C., "Chemical Reactions," Signifi- cance of Tests and Properties of Concrete and Concrete Making Materials, ASTM STP 169-A, 1966.
  27. Highway Research Board, "Properties of Concrete," Highway Research Record No. 43, 1963.
  28. Mehta, P. K. and Paulo J. M. Monteiro, "Concrete-Structure, Properties and Materials," 2nd edition, 1993.
  29. CEB-FIP, "Model Code for Concrete Structures," 1990.

Cited by

  1. System Melting Compound vol.25, pp.2, 2013, https://doi.org/10.4334/JKCI.2013.25.2.209
  2. Development of Concrete and Evaluation of Properties of Combined Steel making Slag Aggregates for Offshore Structure Production (I) vol.25, pp.2, 2016, https://doi.org/10.7844/kirr.2016.25.2.49