Abstract
In order to verify the effect of embedded type sacrificial anode system, accelerated tests in the presence or absence of some chloride content and cracks were carried out. The half-cell potential, potential-decay and corrosion ratio of reinforcing steel in concrete specimen were measured to evaluate the effectiveness of the system. From the test results, the application of the system led to the satisfaction on NACE's criterion in all mixtures of concrete. Additionally it was found that only 10% of steel bar area was corroded due to the application of the system, while comparable 30% of steel bar area was corroded in concrete with no protection system. Based on the results of this investigation, it can be concluded that the criterion of potential-decay is more effective standard than that of protection potential, when the embedded sacrificial anode system is applied on marine concrete structures.
해양환경하의 간만대 및 해상 대기부에 건설되는 콘크리트구조물 중 철근부식 억제를 위한 연구의 일환으로 매설형 희생양극재의 효과에 대하여 고찰하였다. 본 연구에서는 염화물 및 균열의 유무에 따른 매설형 희생양극재를 적용한 철근콘크리트 공시체를 제작하여 3% NaCl 용액으로 촉진시험을 실시하여 방식전위, 복극량 및 부식면적률을 평가하였다. 매설형 희생양극재를 적용한 콘크리트 공시체의 부식면적률을 평가한 결과, 10% 정도의 공식(Pitting corrosion)만이 발생하였으나, 적용하지 않은 공시체의 경우에는 30% 이상의 녹(Rust)이 발생되었다. 이때, 매설형 희생양극재를 적용한 공시체의 방식전위는 -850 mV(vs. CSE)이하의 기준에는 미달하였으나 NACE의 복극량 기준 100mV이상을 만족하였다. 따라서 이상의 연구 실험결과를 종합하면 매설형 희생양극재를 철근콘크리트구조물용 방식재료로 적용할 경우 방식성능의 판단 기준으로 방식전위 보다는 복극량 측정 결과를 기초로 평가하는 것이 타당할 것으로 사료된다.