Fatigue Crack and Delamination Behavior in the Composite Material Containing n Saw-cut and Circular Hole (I) - Aramid Fiber Reinforced Metal Laminates -

소컷 및 원공 주위의 피로균열 형태변화와 층간분리거동 (I) - 아라미드섬유 강화 금속적층재의 경우 -

  • 송삼홍 (고려대학교 기계공학과) ;
  • 김철웅 (고려대학교 대학원 기계공학과)
  • Published : 2003.01.01
Download PDF
⟨ Previous Next ⟩

Abstract

The aramid fiber reinforced metal laminates(AFRMLs) used for the wing part fair flight suffer the cyclic bending moment of variable amplitude during service. The fatigue crack propagation and delamination behavior in AFRMLs containing a saw-cut and circular hole was investigated using the average stress criterion(ASC) model. Mechanical tests were carried out using the cyclic bending moment of 4.9 N . m and delamination was observed by ultrasonic C-scan images. In case of AFRMLs containing a saw-cut fatigue crack propagated in aluminum matrix, inducing delamination. However, in case of AFRMLs containing a circular hole, delamination formed with two types under cyclic bending moment of 4.9 N . m. First, delamination formed along the fatigue crack in aluminum matrix. Second, delamination formed without any fatigue crack around the circular hole. Therefore, delamination was formed depending on the stress distribution near the circular hole.

Keywords

References

  1. Jung-Ho Kwon, 1990, 'The Analysis of Damage Tolerance in Aircraft Structural Design,' Journal of the KSME, Vol. 30, No.2, pp. 131-140
  2. Gunnink J. W., Verbruggen M. L. C. E. and Vogelesang L. B., 1984, 'ARALL, A Light Weight Structural Material For Impact and Fatigue Sensitive Structures,' The 10th European Rotorcraft Forum, The Hague, The Netherlands, pp. 241-254
  3. Marissen R., 1988, 'Fatigue Crack Growth in ARALL : A Hybrid Aluminum-Aramid Composite Material : Crack Growth Mechanism and Quantitative Prediction of the Crack Growth Rates,' Ph. D. Thesis, Delft University of Technology, Netherlands
  4. Lin C. T., Kao P. W. and Yang F. S., 1991, Composite, Vol. 2, p. 135
  5. Macheret J., Teply J. L. and Winter E. F. M., 1989, Polymer Composites, Vol. 10, p. 322 https://doi.org/10.1002/pc.750100508
  6. Guo Y. J. and Wu X. R., 1999, 'Bridging Stress Distribution in Center-cracked Fiber Reinforced Metal Laminates : Modeling and Experiment,' Engineering Fracture Mechanics, Vol. 63, pp. 147-163 https://doi.org/10.1016/S0013-7944(99)00018-1
  7. Yon-Jig Kim and Jae-Kyoo Lim, 2001, 'A Study on Fatigue Crack Propagation Mechanism of GFRP in Synthetic Sea Water,' KSME International Journal, Vol. 15, No. 10, pp. 1380-1385
  8. Sam-Hong Song and Cheol-Woong Kim, 2001, 'The Delamination and Fatigue Crack Propagation Behavior in A15052/AFRP Laminates Under Cyclic Bending Moment,' Transactions of the KSME, A, Vol. 25, No.8, pp. 1277-1286
  9. Akbar Afaghi-Khatibi and Lin Ye, 1997, 'Residual Strength Simulation of Fiber Reinforced Metal Laminates Containing a Circular Hole,' Journal of Composite Materials, Vol. 31, No. 19, pp. 1884-1904 https://doi.org/10.1177/002199839703101901
  10. Glyn Lawcock, Lin Ye and Yiu-Wing Mai, 1997, 'Progressive Damage and Residual Strength of a Carbon Fiber Reinforced Metal Laminate,' Journal of Composite Materials, Vol. 31, No.8, pp. 762-787 https://doi.org/10.1177/002199839703100802
  11. Sam-Hong Song and Cheol-Woong Kim, 2001, 'The Mixture Ratio Effect of Epoxy Resin, Curing Agent and Accelerator on the Fatigue Behavior of FRMLs,' Transactions of the KSME, A, Vol. 25, No.4, pp. 592-601
  12. Nuismer R. J. and Whitney J. M., 1975, 'Uniaxial Failure of Composite Laminates Containing Stress Concentrations,' Fracture Mechanics of Composites, ASTM STP 593, p. 117