Abstract
This study is intended to analyze the effectiveness of expansive additive, shrinkage reducing agent and combination of the two to reduce the autogenous and drying shrinkage of high performance concrete using mineral admixture such as fly ash, blast furnace slag powder and silica fume. According to results, when expansive additive and shrinkage reducing agent are mixed within an appropriate mixing ratio, fluidity and air content are not influenced, and the enhancement of compressive strength is favorable at the age of 91 and 180days. At the mixing ratio of expansive additive of 5% and 10%, the autogenous and drying shrinkage is reduced by 32∼68% and 25∼49% respectively in comparison with plain concrete. And they are reduced by 18∼34% and 16∼26% respectively at the mixing ratio of shrinkage reducing agent of 0.5% and 1.0%, compared with plain concrete. The mixture of EA-SR combined with expansive additive and shrinkage reducing agent is most effective for reduction of shrinkage. Therefore, it is considered that the using method in combination with expansive additive and shrinkage reducing agent is effective to reduce the shrinkage of high performance concrete using mineral admixture such as fly ash, blast slag powder and silica fume.
본 연구에서는 플라이애쉬, 고로슬래그 미분말 및 실리카 퓸 등 광물질 혼화재를 사용하는 고성능 콘크리트에서 자기 및 건조수축을 저감하기 위한 방안으로 팽창재, 수축저감제 및 팽창재와 수축저감제를 병용 사용하는 것에 대하여 분석하였다. 실험결과, 팽창재 및 수축저감제 혼입은 적정 혼입률 범위내에서 유동성 및 공기량에 큰 영향을 미치지 않는 것으로 분석되었으며 재령 91, 180일의 강도발현도 양호한 것으로 나타났다. 또한, 팽창재 5%, 10%에서는 플레인 콘크리트와 비교하여 자기수축을 32∼68%, 건조수축은 25∼49% 감소하는 것으로 나타났고, 수축저감제 혼입률 0.5%, 1.0%에서는 플레인 콘크리트와 비교하여 자기수축은 18∼34% 및 건조수축은 16∼26% 저감하는 것으로 나타났다. 특히, 팽창재와 수축저감제를 병용한 경우의 EA-SR배합에서는 수축저감의 효과가 가장 우수한 것으로 나타났다. 따라서 플라이애쉬, 고로슬래그 미분말 및 실리카 퓸 등 광물질 혼화재를 사용한 고성능 콘크리트의 수축을 저감시키기 위해서는 팽창재와 수축저감제를 병용 사용하는 것이 효과적인 것으로 판단된다.