Abstract
Recycling of aluminum dross is an important issue in the secondary aluminum industries. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing alumina refractories. Sample dross was classified according to its size. The dross smaller than 1 mm was leached with sodium hydroxide solution to extract the remained aluminum from the dross into the solution. and then aluminum hydroxide precipitate was recovered from the leach liquor. The waste residue in the leaching was washed, dried and roasted. Most remained metallic components in the residue was changed into oxide through the processes. The roasted dross was made into alumina castable refractories by mixing with aggregates and a binder. Bending strength of the tested castable specimen was over $25\;kg/\textrm{m}^2$ and compressive strength over $80\;kg/\textrm{cm}^2$, which satisfied the Korean Standard value respectively. From the results, it was suggested that this process could be applicable to recycling of aluminum dross.
알루미늄드로스의 재활용은 알루미늄 재생지금 제조시에 요구되는 중요한 사항 중의 하나이다. 본 연구에서는 국내 재생 알루미늄업체에서 발생된 알루미늄드로스를 처리하여 알루미나질 내화물 원료로 재활용하고자 하였다. 드로스 시료를 크기에 따라 선별하고, 1 mm보다 작은 크기의 드로스를 수산화나트륨 용액으로 침출하여 드로스 중의 잔류 알루미늄을 용액 중으로 분리 추출하고, 침출용액에서 석출반응에 의하여 수산화알루미늄을 회수하였다. 드로스 중의 금속알루미늄을 회수한 후 발생된 침출잔사는 수세, 건조, 배소와 같은 일련의 처리를 하여 드로스 중의 잔류 금속성분을 산화물 형태로 변환시켰다. 배소 처리한 드로스 잔사를 골재 및 점결제와 배합하여 알루미나질 캐스타블내화물을 만들고, 굽힘강도와 압축강도를 시험한 결과 KS 기준치인 굽힘강도 $25\;kg/\textrm{m}^2$ 이상, 압축강도 $80\;kg/\textrm{cm}^2$ 이상을 만족하였다. 본 연구결과를 알루미늄드로스를 효율적으로 재활용할 수 있는 한가지 방안으로 제안하고자 한다.