Abstract

Normally coating is used a method for protecting reinforced concrete. For this purpose, organic as well as inorganic coatings are used. The advantages of inorganic coatings are lower absorption of UV, non-burning etc. On the other hand, organic coatings have the advantage of low permeability of $CO_2$, $SO_2$ and water. Organic coatings provide better protection for reinforced concrete. However, in organic coatings such as epoxy, urethane and acryl, long-term adhesive strength is reduced and the formed membrane of those is blistered by various causes. Also when organic coatings are applied to the wet surface of concrete, they have a problem with adhesion. So, we developed coating material, WGS-Eco which was hybridized with polymer and cement based material to protect concrete structures and solve problems of organic coatings. This study was conducted an comparative evaluation on physical and durable performance of developed coating material and previously used coating materials. As a result, the performance of developed coating material was not inferior to organic coating materials. So, the developed coating material was considered as a suitable coating material which had advantages of inorganic and organic coatings for protecting concrete.

일반적으로 코팅은 철근 콘크리트를 보호하기 위한 방법으로 사용되어 진다. 이러한 목적으로 사용되어지는 코팅에는 무기계 코팅뿐만 아니라 유기계 코팅이 있다. 무기계 코팅의 장점은 낮은 자외선 투과성과 불연성 등이다. 반면, 유기계 코팅의 장점은 이산화탄소, 이산화황 및 물 등의 낮은 투과성이며 무기계 코팅보다 더 우수한 철근 콘크리트 보호성능을 가지고 있다. 그러나 에폭시, 우레탄 및 아크릴과 같은 유기계 코팅은 여러 가지 원인에 의해 장기 접착강도가 감소되고 형성된 코팅 막의 들뜸이 발생된다. 또한 유기계 코팅이 콘크리트의 습한 표면에 적용될 경우 접착의 문제점을 갖고 있다. 따라서, 콘크리트 구조물을 보호하고 유기계 코팅의 문제점을 해결하기 위해 폴리머와 시멘트계 재료를 합성시킨 코팅재(WGS-Eco)를 개발하였다. 본 연구에서는 개발된 코팅재와 이전에 사용되었던 코팅재의 물리 성능 및 내구 성능을 평가하였으며, 그 결과 개발된 코팅재는 유기계 코팅재에 비해 성능이 뒤떨어지지 않았다. 따라서 개발된 코팅재는 유기계와 무기계 코팅의 장점을 갖으면서 콘크리트를 보호하기 위한 적합한 코팅재라고 판단되었다.

Keywords

• inorganic coating;
• organic coating;
• hybridize;
• protecting concrete