Abstract

This study was carried out to investigate the mechanical properties of fabric E-glass fiber reinforced laminated timber. Specimens used to Korean red pine(Pinus densiflora) and Japanese larch(Larix kaemferi). Fabric E-glass fiber was inserted in the solid wood with aqueous polymer-isocyanate resin(MPU-500). The results were as follows: 1. Aqueous polymer-isocyanate resin(MPU-500) was good resin to manufacture laminated timber. specially, it was satisfied to property standard of construction laminated timber(KS F 3021) except for two ply glass fiber. 2. Bending and shear strengths of solid wood inserted with fabric glass fibers were not different from control solid wood. But, proportional limit bending stress was increased following the number of fabric glass fibers. Therefore, it was considered that to improve the bending and shear strength of fabric glass fiber reinforced laminated timber, the glass fiber thickness and its mesh should be modified to fitness following working conditions.

본 연구는 국산소경재인 소나무(Pinus densiflora)재와 낙엽송(Larix kaemferi)재로 제조된 유리섬유강화 집성재의 강도적 성질을 조사해 보기 위하여 실시되었다. 먼저, 직물 유리섬유를 수성고분자-이소시아네이트계(MPU-500) 접착제를 사용하여 control재와 유리섬유를 각각 1층과 2층 함입하였다. 본 연구의 결과는 다음과 같다. 1. 수성고분자-이소시아네이트 수지는 집성재 제조용으로 적합하였으며, 특히 유리섬유를 2층 함입한 소재를 제외하고는 구조용 집성재의 품질기준(KS F 3021)을 만족시켰다. 2. 직물유리섬유를 함입할 경우 휨강도, 전단강도에서 control재보다 크게 뛰어나지는 않았지만, 비례한도 휨응력은 유리섬유의 함입 층수에 비례하여 증가하였다. 그러므로, 직물 유리섬유의 mesh수와 두께를 집성재 소재의 형태에 따라 적절히 조정한다면, 휨강도와 전단강도를 좀더 향상시킬 수 있을 것으로 판단되었다.

Keywords

• laminated timber;
• fiber glass;
• aqueous polymer-isocyanate resin(MPU-500);
• lamination