Cheong, Cheong-Jo;Kim, Young-Kyu
정정조;김영규
The engineering characteristics of recycled plastics (low density polyethylene:LDPE) filled with sludge ash in accordance with various content ratio of the ash are investigated. Specific conclusions derived from this study are as follows. The results of the absorption ratio and specific gravity were increased according to the ash content. The improvement in the compressive, tensile, bending strength is remarkable based on the standard design strength of concrete aged 28days. The specimens which were filled with 30 percent sludge ash appear to have the highest strength. Therefore, it is possible to produce the construction materials using these materials substitute for the concrete. The Melt Flow Index(MFI) is closely associated with the plasticity. In this work, the MFI of the specimens without ash is 4.90 g/10min and decreases to 0.08 g/10min according to ash addition 50 percent.
본 연구는 폐기물 재활용의 일환으로 슬러지 소각재를 재생 플라스틱(저밀도 폴리에틸렌)의 충진제로 혼입한 재료의 공학적 특성을 평가한 결과, 다음과 같은 결론을 얻을 수 있었다. 물리적 시험 결과에 있어서 소각재 함유량이 증가함에 따라서 비중 및 흡수율 시험 결과 또한 증가하였다. 압축강도, 인장강도, 휨강도는 콘크리트의 28일 강도를 모두 상회하였으며, 동결?가온후의 강도 또한 콘크리트의 28일 강도보다 높은 결과 값을 나타냈다. 제지 폐수슬러지 소각재를 30%혼합한 재료가 가장 높은 강도 값을 나타내었다. 따라서 제지 폐수슬러지와 재생플라스틱을 혼합한 재료를 콘크리트의 대용품으로서 충분이 그 활용이 가능하리라 판단된다. 용융지수는 플라스틱 제품의 성형성과 밀접한 관계가 있다 소각재를 혼입하지 않았을 경우에 용융지수가 4.9 g/10min이었으나, 소각재를 50% 혼입하였을 경우에는 0.07 g/10min의 결과를 나타내었다.