Abstract
The sulfuric acid pressure leaching of artificial matte which was similar to the matte prepared from manganese nodules was carried out to investigate the extraction behaviors of copper, nickel, cobalt and iron. The effects of sulfuric acid concentration, leaching time, temperature and oxygen pressure were studied. The extractions of copper, nickel and cobalt were over 98% by 10kg/cm2 oxygen pressure leaching with 1.0%(v/v) H2SO4 and 25g/500ml pulp density at 150℃, 2 hours. At this condition, iron was extracted only 1.4% with precipitated as hematite. The leaching of iron increased with increase of H2SO4 concentration due to high acidity of solution. The leaching temperature and oxygen pressure give little effects on leaching of nickel and cobalt while great on copper.
망간단괴로부터 제조되는 매트상과 유사한 합성 (Cu-Ni-Co-Fe)매트상을 제조하여 고온고압하에서 황산에 의한 구리, 니켈, 코발트 그리고 철의 침출특성을 조사하기 위해 황산농도, 반응시간, 반응온도, 산소압이 유가금속들의 침출율에 미치는 영향을 검토하였다. 고액농도 25g/500㎖에서 황산농도 1.0%(V/V), 산소압력 10 ㎏/㎠, 반응온도 150℃ 그리고 반응시간 이 2시간의 경우 니켈, 코발트 그리고 구리 모두 98% 이상 침출되었으며 철은 1.4%가 용해되었다. 황산농도가 1.0% (v/v)보다 높으면 침출액의 pH가 낮아져 철의 침출율이 급격히 증가하였다. 니켈과 코발트의 침출율은 침출온도와 산소압력에 별 영향을 받지 않으나 구리는 큰 영향을 받았다.