Luminescence Characteristics of Sr3MgSi2O8：Eu Blue Phosphor for Light Emitting Diodes

LED용 Sr3MgSi2O8：Eu청색 형광체의 발광특성

  • 최경재 (한국화학연구원 화학소재연구부) ;
  • 박정규 (한국화학연구원 화학소재연구) ;
  • 김경남 (한국화학연구원 화학소재연구) ;
  • 김창해 (한국화학연구원 화학소재연구) ;
  • 김호건 (한양대학교 응용화학과)
  • Published : 2004.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

We have synthesized a Eu$^{2＋}$-activated Sr$_3$MgSi$_2$ $O_{8}$ blue phosphor and investigated an attempt to develop blue LEDs by combining it with a InGaN blue LED chip (Len=405 nm). The InGaN-based Sr$_3$MgSi$_2$ $O_{8}$：Eu LED Lamp shows two bands at 405 nm and 460 nm. The 405 nm emission band is due to a radiative recombination from a InGaN active layer. This 405 nm emission was used as an optical transition of the Sr$_3$MgSi$_2$ $O_{8}$：Eu phosphor. The 460 m emission band is ascribed to a radiative recombination of Eu$^{2＋}$ impurity ions in the Sr$_3$MgSi$_2$ $O_{8}$ host matrix. As a consequence of a preparation of W blue LED Lamp using the Sr$_3$MgSi$_2$ $O_{8}$：Eu blue phosphor, the highest luminescence efficiency was obtained at the ration of epoxy/blue phosphor(1/0,202). At this time, the CIE chromaticity was x=0.1417 and y=0.0683.

Eu$^{2＋}$를 활성제로 Sr$_3$MgSi$_2$ $O_{8}$ 청색 형광체를 합성하고, Sr$_3$MgSi$_2$ $O_{8}$：Eu 청색 형광체를 InGaN의 UV chip에 도포하여 청색 LED Lamp를 제조하였다. 제조된 청색 LED Lamp는 405nm와 460nm에서 두 개의 파장을 나타내고 있다. 405nm의 파장은 InGaN의 활성영역으로부터의 radiative recombination 때문에 나타나는 피크이다. 여기에서 나오는 405nm의 발광은 본 Sr$_3$MgSi$_2$ $O_{8}$：Eu 청색 형광체의 여기원으로 사용된다 460nm에서의 발광 밴드는 Sr$_3$MgSi$_2$ $O_{8}$ 모체내에서 Eu$^{2＋}$ 이온의 radiative recombination에 의한 것이다. 발광효율이 좋은 Sr$_3$MgSi$_2$ $O_{8}$：Eu 청색 형광체를 이용하여 UV 청색 LED Lmp를 제조한 결과, 에폭시와 청색 형광체의 무게 비율이 1$.$0.202에서 가장 좋은 광도값을 얻을 수 있었다. 이때 색좌표는 CIE x=0.1417, CIE y=0.0683이었다.

Keywords

References

  1. Electronic Display Light Emitting Diode Display M. Shoichi
  2. Bull. of the KIEEME v.14 no.11 White-Light Development Technology Trend S. J. Sohn
  3. Bull. of the KIEEME v.14 no.11 The Latest Research Trend of White-Emitting LEDs for Semiconductor Illumination C. H. Hong
  4. J. Electrochem. Soc. v.115 Equilibria and $Eu^{2+}$ Luminescence of Subsolidus Phases Bounded by $Ba_3MgSi_2O_8$, Sr$_3MgSi_2O_8$, and Ca$_3MgSi_2O_8$ L. Barry https://doi.org/10.1149/1.2411413
  5. J. Alloys and Comp. v.241 Luminescence of $Eu^{2+}$ in Silicate Hast Lattices with Alkaline Earth Ions in a Raw S. H. M. Poort;H. M. Reijnhoudt;H. O. T. van Kuip;G. Blasse https://doi.org/10.1016/0925-8388(96)02324-9
  6. J. Lumin. v.72 The Influence of the Host Lattice in the Luminescence of Divalent Europium S. H. M. Poort;G. Blasse https://doi.org/10.1016/S0022-2313(96)00360-2
  7. Chem. Mater. v.7 Luminescence of $Eu^{2+}$ in Barium and Strontium Aluminate and Gallate S. H. M. Poort;W. P Blokpoel;G. Blasse https://doi.org/10.1021/cm00056a022
  8. J. Electrocem. Soc. v.115 Fluorescence of $Eu^{2+}$ -Activated Phases in Binary Alkaline Earth Orthosilicate Systems T. L. Barry https://doi.org/10.1149/1.2410935
  9. J. Alloys and Comp. v.260 Optical Properties of $Eu^{2+}$ -Activated Orthosilicates and Orthophos-Phates S. H. M. Poort;W. Janssen;G. Blasse https://doi.org/10.1016/S0925-8388(97)00140-0
  10. J. of the KIIEE Optical Design of RGB LED Cluster Lamps W. H. Kim;I. S. Yeo
  11. An Introduction to Luminescent of Solids H. W. Leverenz
  12. J. Chem. Phys. v.21 A Theory of Sensitized Luminescence in Solids D. L. Dexter https://doi.org/10.1063/1.1699044

Cited by

  1. long afterglow phosphors synthesized solid state reaction and polymerized complex method vol.26, pp.5, 2016, https://doi.org/10.6111/JKCGCT.2016.26.5.193