Abstract

The bored pile is widely used as a low noise and vibration piling method in Korea. However, there is design tendency to minimize the friction capacity of the bored pile because of uncertainty and the quality control specification is not set up. This research analysed the strength characteristics of cement paste after the uniaxial compression test with various condition. Test results show that the compressive strength of cement paste with w/c=0.83 was up to $156.0kgf/cm^2$, and the lower w/c ratio and the longer age, the strength of cement paste increased. Also the higher soil mixing ratio, the strength of soil cement decreased, and too high soil mixing ratio caused the malfuction of soil cement. Also this research analysed the 188 dynamic pile test results which were performed before and after hardening of cement paste. Analysis result showed that the average ultimate unit friction capacity was $9.1tf/m^2$ and this result surpassed the common design criteria of the bored pile.

국내에서는 저소음, 저진동 말뚝공법으로 매입말뚝공법이 매우 활발하게 사용되고 있으나 설계시 마찰지지력을 과소하게 산정하는 경향이 있으며 시멘트풀의 배합비 및 품질관리에 대한 기준이 정립되지 않은 문제점이 있다. 본 연구에서는 시멘트풀에 대해 다양한 조건별로 시험을 실시하여 강도특성을 분석하였다. 시험결과 표준배합비(w/c=83%)의 시멘트풀의 압축강도는 최고 $156.0kgf/cm^2$를 나타내었고 w/c가 낮을수록, 재령이 길수록 압축강도가 커지는 경향을 나타내었고 토사의 혼입률이 높을수록 강도가 감소하여 일정량 이상이 혼입되면 제역할을 하지 못하는 것으로 나타났다. 또한 매입말뚝의 마찰특성을 분석하고 적합한 설계방안을 도출하기 위하여 시멘트풀의 경화 전후에 188회 동재하시험 결과를 분석하였다. 분석결과 극한단위 마찰력은 평균 $9.1kgf/cm^2$을 나타내어 매입말뚝의 통상적인 설계기준을 상회하는 것으로 나타났다.

Keywords

• Bored Pile;
• Bearing Capacity;
• Cement Paste;
• Quality control;
• Design Criteria

• 매입말뚝;
• 지지력;
• 시멘트풀;
• 재하시험;
• 품질관리;
• 설계기준;