Abstract
The electromagnetic properties and microstructures of the basic composition of (Ni$\sub$0.2/Cu$\sub$0.1/Zn$\sub$0.2/)$\sub$0.5/ (Fe$_2$O$_3$)$\sub$0.5/ were invested by changing of SO$_4$, Cl and NO$_3$ series. We were prepared by coprecipitation method and sintered at temperatures 950$^{\circ}C$, 1150$^{\circ}C$, l350$^{\circ}C$, respectively. When sintering at temperature 950$^{\circ}C$, Cl and NO$_3$ series became perfection sintering. On the other hand, SO$_4$ series showed perfection sintering at temperature 1150$^{\circ}C$. According to particle size analysis result, higher magnetic permeability and magnetization value were observed by Cl series than SO$_4$ or NO$_3$ series.
(Ni$_{0.2}$Cu$_{0.1}$Zn$_{0.2}$)$_{0.5}$(Fe$_2$O$_3$)$_{0.5}$의 기본조성으로 공침법에 의해 NiCuZn ferrite를 제조하였으며, ferrite 분말 제조시, SO$_4$, Cl과 NO$_3$ 각 계열별로 분말을 얻어 시편을 제조하였고, 시편을 각각 9$50^{\circ}C$, 11$50^{\circ}C$, 13$50^{\circ}C$에서 소결하여 자기적 특성 및 미세구조를 조사하였다. 9$50^{\circ}C$ 소결시 Cl계열과 NO$_3$계열 분말로 제조된 시편은 완전소결 되었지만 SO$_4$계열로 제조된 시편은 11$50^{\circ}C$에서 완전 소결 형태를 보였다. Cl계열 분말로 제조된 시편이 입도분석결과 다른 두 시편 보다 미분말 특성이 뛰어났으며, 비교적 높은 투자율과 자화값을 나타내었다.