Abstract

In this paper, the hydrogen osmosis test and the mechanical tensile test were carried out to examine hydrogen cracking behavior of STS444 with welding conditions. In $0.5MH_2SO_4+0.001M \;As_2O_3$ solution, the hydrogen embrittlement characteristics of weld zone of STS444 added to load of $1,400 kg/cm^2$ together with hydrogen osmosis by current of $30mA/cm^2$ for 60 min. was considered. As a result of study on the hydrogen embrittlement and mechanical characteristics of STS444외와 with welding conditions the tensile stress and elongation of STS444 get lower by the absorption of oil or water before welding. Also, the reduction rate of tensile stress and elongation of STS444 is larger because of hydrogen embrittlement by the absorption of oil or water. STS444 by the absorption of water before welding is more sensitive to hydrogen embrittlement than oil.

스테인리스 강재인 STS444에 있어서 용접조건에 따른 수소취성 거동을 고찰하고자 수소침투실험과 기계적 인장시험을 실시하였다. 즉, $0.5MH_2SO_4+0.001M \;As_2O_3$ 수용액 중에서 $1,400 kg/cm^2$의 하중을 부가하는 동시에 전기화학 부식시험 장치로 $30mA/cm^2$전류를 60분간 인가하여 수소를 침투시킨 후 기계적 인장시험을 통해서 STS444용접부의 수소취성 특성에 관해서 고찰하였다. STS444에 있어서 용접조건이 수소취성에 미치는 특성을 연구한 결과, 용접 전 기름이나 물의 흡착에 의해 인장강도나 연신율은 낮아진다. 또한 기름이나 물이 흡착함으로써 수소취성에 의한 인장응력 및 연신율의 감소율은 더 크게 나타나고, 용접 전 물의 흡착이 기름의 흡착보다 수소취성에 민감하다.

Keywords

• Boiler;
• Stainless steel;
• Hydrogen embrittlement;
• Cathodic polarization