Abstract

Recently, as the concrete structures are becoming bigger, higher, longer and more special, high strength concrete is demanded. But the fracture behavior of high strength concrete is shown more brittle than that of the normal strength concrete. Therefore, in order to improve the brittle fracture behavior and crack propagation resistance, ACI Committee363 has been recommend the use of fiber reinforced concrete which showed superior property against the crack propagation resistance. On the other hand, bridges, concrete pavements and railroads etc. have been exposed to the repetition loading at least several million times during the service life. Therefore, fatigue load is dominantly most of all, but it is very difficult to estimate the suitable fatigue strength calculated by fatigue load. In this research, in order to examine the fatigue behavior of hybrid fiber reinforced high strength concrete, the static and fatigue tests were carried out. And from these results, it was estimated the fatigue strength of hybrid fiber reinforced high strength concrete.

최근들어 콘크리트 구조물이 대형화, 고층화, 장대화 및 특수화 됨에 따라 고강도콘크리트의 사용이 요구되고 있으나 고강도콘크리트는 일반강도콘크리트 보다 취성적인 파괴거동을 나타내고 있다. 따라서 취성적인 파괴 특성을 개선하고 균열성장 저항성을 증진시키기 위하여 ACI 363 위원회에서는 섬유보강콘크리트의 사용을 추천하고 있다. 한편, 교량 및 콘크리트 포장 등은 공용기간중에 적어도 수백만회 이상의 반복하중을 받고 있어 피로하중이 지배적이나 이에 대한 피로거동 및 피로강도의 규명이 어려운 실정이다. 본 연구에서는 하이브리드섬유보강 고강도콘크리트의 피로거동과 피로강도를 규명하기 위하여 정적 및 피로시험으로부터 구한 반복회수와 중앙처짐과의 관계를 비교분석 하였으며 S-N선도로부터 피로강도식을 제안하였다.

Keywords

• Fatigue Behavior;
• Hybrid Fiber;
• High Strength;
• S-N Diagram;
• Fatigue Strength

• 피로거동;
• 하이브리드섬유보강;
• 고강도;
• S-N선도;
• 피로강도;