Abstract
The purpose of this study is to recycle the fly ash to the valuable resources and settle environment problems which was caused by the fly ash produced from the thermal power plant. Making the fly ash-cement matrix reused fly ash in large quantities, we looked into minutely the physical properties - the elastic modulus, the compressive strength and the drying shrinkage etc - to increase the usefulness as the building materials for the structure widely. In this paper, the variables are the water-binder (39, 42, 45%), the fine aggregate ratio (37, 41, 45%). Because the fracture energy is influenced by the strength, it is showed to decrease with the increase of W/B and S/a. Besides, we will be able to know that basic properties of the fly ash-cement matrix are similar to that of concrete.
화력발전소 산업 부산물인 석탄회(FA)를 재활용하기 위하여 비소성 공법으로, 단위시멘트량의 90%를 석탄회로 대체한 콘크리트 공시체를 제작하여 강도발현 메카니즘을 규명하고, 기초적인 물성시험으로 재령별 압축강도와 탄성계수, 노치별 3점 휨강도 실험을 실시하였다. 본 연구에서는 변수를 W//(F+C) 39, 42, 45%, S/a 37, 41, 45%로 하여 경화체의 휨강도를 측정한 결과 물-결합재비, 잔골재율이 증가 할수록 파괴에너지가 감소하였으며, 압축강도와 정탄성계수 측정결과, 일반콘크리트의 약 75%정도로서 일반콘크리트에 비해선 역학적특성이 다소 취약하지만 벽돌이나 블록등 일부 프리캐스트 콘크리트제품에는 충분히 사용가능한 것으로 나타났다.