Abstract

In the study of foaming a general waste glass, sample 1 to 5 were made in a various foaming conditions, measurements of pH, density, compressive strength, thermal conductivity, and the sound absorption rate were carried out. Sample I showed the most small pore, and sample 5 showed pores of 3 times larger than that of sample 1. In terms of pore size, Sample 5 was foamed mostly well, but except lower density compressive strength, efficiency of sound absorption, testing in sound room were obtained below the minimum values is lower. In the case of Sample 1 it showed $0.58g/cm^3$, but the final target value was $0.8g/cm^3$. In the case of compressive strength it showed $22kg/cm^3$, which is above value of the final target. The efficiency of sound absorption of Sample 1 showed NRC 0.68, which is close to the final target of NRC 0.7.

본 연구에서는 폐유리를 여러 가지 조건으로 시편 1에서 5까지 발포실험을 하여 발포유리의 pH, 밀도, 열전도, 압축강도 그리고 흡음률을 측정하였다. 시편별 pore크기는 시편 1의 Pore가 가장 적게 발포되었고, 시편 5의 경우 pore크기가 시편 1보다 3배 이상 크게 발포되었다. pore크기가 시편 5에서 가장 크게 발포되었지만, 밀도가 낮은 것 외에는 압축강도와 흡음률의 결과가 최종목표에 미달하였고, 시편 1의 경우에는 밀도가 최종목표 $0.8g/cm^3$ 보다 우수한 $0.58g/cm^3$로 나타났고, 압축강도의 경우도 최종목표보다 높은 $22kg/cm^3$로 나타났으며, 흡음재로서의 흡음률은 시편 1의 경우 NRC 0.68로서 최종목표인 NRC 0.7에 근접하는 결과를 얻었다.

Keywords

• recycling waste glass;
• foaming glass