Abstract
It is known that latex-modified concretes were increased their durability and permeability by added latex. The purpose of this study was to analysis the air void systems in latex-modified concretes using a reasonable and objective image analysis method with main experimental variables such as water-cement ratios, latex contents(0%, 15%) and cement types(ordinary portland cement, high-early strength cement and very-early strength cement). The results are analyzed spacing factor, air volume after hardened, air distribution and structure. Also, air void systems and permeability of latex-modified concretes were compared with correlation. The results are as follows; The same w/c ratio LMC showed better air entraining effect than OPC with AE water reducer. The VES-LMC showed that the number of entrained air below $100{\mu}m$ increased more than four times. In the HES-LMC, micro entraining air having range from 50 to $500{\mu}m$ increased above 7 times without antifoamer. Though spacing factor was measured low, latex-modified concretes were showed that permeability was good. It is considered that air void system does not have an effect on the property of latex-modified concretes but latex film is more influenced in the their durability.
라텍스개질 콘크리트는 라텍스의 첨가로 인하여 콘크리트의 내구성을 개선하는 것으로 알려져 있으며, 투수저항성이 크게 향상되는 것으로 연구되었다. 본 연구에서는 SBR 라텍스 혼입에 따른 콘크리트 내부 공극 구조의 변화를 연구하고자 화상분석법을 이용하여 라텍스개질 콘크리트의 W/C비, 라텍스 함량, 시멘트 종류에 변화를 주어 간격계수, 경화 후 공기량, 공극 직경에 따른 공극 분포 및 공극 구조 상태 분석 등을 파악하였다. 또한, 라텍스 첨가에 따른 내부 공극 구조 특성과 투수저항성과의 상관성을 비교하였다. 라텍스개질 콘크리트는 내부 공극 분석 결과, 동일 물-시멘트비 조건에서 AE감수제를 사용한 OPC에 비해 더 우수한 연행공극 효과가 있는 것으로 분석되었다. 초속경시멘트는 $100{\mu}m$ 미만의 연행공극의 수가 4배 이상 증가하였다. 조강 시멘트는 SBR 라텍스로 인하여 $50{\sim}500{\mu}m$ 범위의 미세 연행 공기량이 약 7배 이상 증가되는 현상을 나타내었다. 그러나 투수성에 있어서는 낮은 간격계수에도 불구하고 높은 투수저항 특성을 나타내었다. 내구성에 있어서 라텍스개질 콘크리트에서는 공극 구조의 영향보다는 라텍스 폴리머 필름에 의한 영향이 더 큰 것으로 판단되었다.