Abstract
This study dealt with correlation analysis of binder stiffness with deformation strength and dynamic creep property of asphalt mixtures for evaluation of applicability of deformation strength $(S_D)$. Two aggregates, with maximum size of 13mm and eight binders were used to produce 16 different mixtures. The stiffness of binder $(G^*/sin\delta)$ was measured using DSR at $64^{\circ}C$. Final deformation(FD) and dynamic stability(DS) were measured by dynamic creep (DC) test, and SD was measured by Kim test for each mixture. Results of correlation analysis between $G^*/sin\delta$, and $S_D$, m and DS showed that correlation with binder stiffness and deformation strength was the highest $(R^2>0.88)$. There was good correlation between DS, FD with $S_D$. The results indicated that rut-resistance property of mixture is better reflected in $S_D$ test than FD or DS of dynamic creep test. Therefore, it is concluded that $S_D$ can be possibly used for evaluation of rut resistance of asphalt concretes with a good reliability if the procedure is standardized.
아스팔트 바인더 Stiffness와 혼합물의 변형강도 및 동적크리프 특성과의 상관성 분석을 토대로 혼합물의 소성변형 저항성 (내변형성) 추정을 위한 Kim test의 적용성을 고찰하였다. 본 연구는 골재 2종류, AC 60-80 및 이를 개질한 총 8종류의 바인더로 총 16가지 혼합물을 제조하였다. DSR로 각 바인더의 $G^*/sine\delta$를 측정하였으며 Kim test의 변형강도와 동적크리프 시험의 최종변위(FD)와 동적안정도(DS)를 각 혼합물로부터 측정하였다. 바인더의 $G^*/sine\delta$와 소성변형 관련 3가지 특성($S_D$. FD, DS)과의 상관성 분석 결과 $G^*/sine\delta$와 $S_D$와 상관성이 가장 높은 것으로 나타났다 $(R^2=0.88)$ 이는 혼합물에 내재해 있는 내변형성의 차이를 Kim test가 더 잘 구분해 낼 수 있음을 의미한다. 또한 DS와 $S_D$의 회귀분석 결과, $R^2$이 약 0.84 이상을 보여 변형강도는 동적크리프 시험의 동적안정도와 좋은 상관성을 가짐을 확인하였다. 따라서 본 연구를 통하여 아스팔트 혼합물의 내변형성 평가시 Kim test의 활용 가능성이 매우 높음을 확인하였다.