Far Infrared Radiation Characteristics of Germanium Compounds

게르마늄 화합물의 원적외선 방사특성

  • Received : 2006.07.12
  • Accepted : 2006.11.20
  • Published : 2006.12.10
Download PDF
⟨ Previous Next ⟩

Abstract

In order to study the effects of $GeO_{2}$ contents in $XSiO_{2}{\cdot}YGeO_{2}$ and $XSiO_{2}{\cdot}YNa_{2}O{\cdot}ZGeO_{2}$ compounds on far infrared ray radiation, we investigated the sample of $XSiO_{2}{\cdot}YGeO_{2}$ and $XSiO_{2}{\cdot}YNa_{2}O{\cdot}ZGeO_{2}$ using TG-DTA, XRD, FT-IR spectrophotometer and FT-IR spectrometer. The far infrared ray emissivity and emission power were increased with the increase of $GeO_{2}$ contents in $XSiO_{2}{\cdot}YGeO_{2}$ and $XSiO_{2}{\cdot}YNa_{2}O{\cdot}ZGeO_{2}$ compounds. The far infrared ray emissivity and emission power of $XSiO_2{\cdot}YGeO_2$ compounds were higher than those of $XSiO_{2}{\cdot}YNa_{2}O{\cdot}ZGeO_{2}$ compounds.

$XSiO_{2}{\cdot}YGeO_{2}$계 화합물과 $XSiO_{2}{\cdot}YNaO_{2}{\cdot}ZGeO_{2}$계 화합물을 제조하고 이들 화합물에서 $GeO_{2}$의 함량을 변화시켜 원적외선 방사율과 원적외선 방사에너지에 미치는 영향을 연구하였다. 제조된 시료의 특징은 TG-DTA, XRD, FT-IR spectrophotometer 그리고 FT-IR spectrometer에 의해 조사되었다. $XSiO_{2}{\cdot}YGeO_{2}$와 $XSiO_{2}{\cdot}YNaO_{2}{\cdot}ZGeO_{2}$계의 화합물은 $GeO_{2}$의 함량이 증가할수록 원적외선 방사율과 방사에너지가 점차적으로 증가하였다. 원적외선 방사율과 방사에너지는 $XSiO_{2}{\cdot}YGeO_{2}$계 화합물의 경우가 $XSiO_{2}{\cdot}YNaO_{2}{\cdot}ZGeO_{2}$계 화합물보다 높게 나타났다.

Keywords

Acknowledgement

Supported by : 상명대학교 자연과학 연구소

References

  1. C. K. Chee, T. S. Choi, and S. I. Jang, J. KIIEE, 16, 7 (2002)
  2. D. K. Lee, Proc. KIIEE, 15, 14 (2001)
  3. J. M. Lee, J. O. Park, and J. S. Choi, J. KIIEE, 18 (1991)
  4. Y. S. Jin, H. Y. Lee, Y. K. Kim, K. R. Kim, and H. J. Lee, J. Korean Soc. Jungshin Sci., 7, 19 (2003)
  5. Y. H. Kim, T. H. Ji, S. Y. Kim, and G. H. Rhee, Korean J. Air-Condition and Refrigeration Eng., 18, 526 (2006)
  6. 高鳥廣夫, 杉山豊彦 , セラミツクス, 23, 263 (1988)
  7. J. H. Choi, J. S. Im, and D. H. Oh, J. Korean Soc. Food Sci. Nutr., 35, 635 (2006) https://doi.org/10.3746/jkfn.2006.35.5.635
  8. 根岸直樹, 菊地眞, セラミツクス, 23, 325 (1988)
  9. 高鳥廣夫, 濟業 協會誌, 10, 373 (1982)
  10. 高鳥廣夫, 工業 奇術, 20, 66 (1972)
  11. 高鳥廣夫, 濟業 協會誌, 10, 373 (1982)
  12. 山本博孝, 二官秀明, 荏業 協會誌, 82, 80 (1981)
  13. T. S. Choi, Industrial Mineralogy Symposium, 46 (1997)
  14. N. J. H, MS. Dissertation, Kyung Hee Univ., Seoul, Korea (1991)