Abstract
The leaching behaviors of zinc and manganese oxides of spent alkaline manganeses battery in sulfuric acid solution by using $H_{2}O_{2}$ as a reducing agent were investigated according to the concentration of $H_{2}SO_{4}$, temperature, reaction time, and the amount of $H_{2}O_{2}$. The experimental results of zinc and manganeses dissolution rates obtained without a reducing agent at 100 g/L solid/liquid ratio, 3.0 M $H_{2}SO_{4}$, $60^{\circ}C$ and 200 r.p.m. were 97.7% and 43.5%, respectively. On the other hand, zinc and manganeses dissolution rates obtained by adding 30 mL reducing agent at $60^{\circ}C$ were 99.6% and 97.1%, respectively. The addition of the reducing agent increased the leaching of manganese by two-fold compared to the absence of a reducing agent. In case of adding over 30 mL $H_{2}O_{2}$, however, the leaching rates of zinc and manganeses were independent of reducing agent amounts.
망간산화물과 아연이 혼재되어 있는 폐알카리 망간전지로부터 황산용액에서 환원제로 과산화수소를 이용하여, 침출제 농도, 온도, 반응시간, 과산화수소의 양 등을 변화시키면서 망간과 아연의 침출거동을 조사하였다. 그 결과 고액농도 100 g/L, 황산농도 3.0 M, 반응온도 $60^{\circ}C$, 교반속도 200 r.p.m. 그리고 과산화수소를 첨가하지 않은 조건에서 아연과 망간의 침출율은 각각 97.7 %와 43.5 %를 나타내었으나, 반응온도 $60^{\circ}C$에서 과산화수소 30 mL를 첨가하였을 때는 아연과 망간의 침출율은 각각 99.6 %와 97.1%를 나타내어 환원제를 첨가하지 않은 조건보다 망간의 침출율이 약 2배 정도 증가하였다. 그러나 과산화수소 양이 30 mL 이상에서는 첨가되는 과산화수소의 양이 증가하여도 아연과 망간의 침출율의 변화는 거의 없었다.