Abstract
This study reports the properties of high early strength & durability of concrete using PC admixture. To apply these data to construction site, we did the lab tests. The target of this study is to accomplish early strength of concrete (5.0 Mpa/18 hr), and we did the durability tests such as length change test, chloride ion penetration test, fleeting and thawing test, adiabatic test, etc. And we tested the porperties of concrete by the different factors, such as the type of admixtures, curing temperature, the amount of binder, etc. Through the test of concrete using the different type of admixture, PC type was more excellent than PNS type admixture. As a result, we made a concrete of high early strength concrete, and excellent durable concrete. According to these tests, we concluded that we can apply this type of PC admixture to the civil & construction site, and we can reduce the term of works and finally we will accomplish the economical construction.
이 연구는 PC계 조강혼화제를 사용한 콘크리트의 조기강도 및 내구 특성에 대한 내용이다. 이들 데이터를 건설현장에 적용하기 위하여 실내 시험을 실시하였다. 이 연구의 목표는 조기강도 즉 재령 18시간에 5.0 MPa의 강도를 확보하기 위하여 진행되었다. 그리고, 건조수축 길이 변화 시험, 염소이온 침투 저항성 시험, 동결융해 저항성 시험, 단열온도 상승 시험 등과 같은 내구성 시험을 실시하였다. 연구를 실시함에 있어 각각의 시험 인자들 즉, 혼화제의 종류, 콘크리트의 양생온도, 결합재의 사용량 등의 시험 인자들을 변수로 하여 각각의 콘크리트의 물성을 확인하였다. 혼화제 종류에 따른 콘크리트의 시험 결과 PC계 혼화제를 사용했을 때 PNS를 사용했을 때보다 훨씬 뛰어난 성능을 발휘한다는 사실을 확인할 수 있었다. 결론적으로 이 연구를 통하여 조기강도를 확보하고, 고 내구성을 확보한 콘크리트를 제조할 수 있었다. 이들 시험을 통하여, 토목 및 건축 현장에서 PC계 조강혼화제를 사용할 수가 있고, 조기강도를 앞당김으로써 공사 기간 단축에 의한 공사 원가 절감으로 경제적인 시공이 가능하였다.