MCM-41을 이용한 LDPE-LLDPE-EVA 공중합체 혼합물의 접촉 열분해 반응에 미치는 Aluminium 첨가 효과

Effect of Aluminium Addition to MCM-41 on Catalytic Cracking of an LDPE-LLDPE-EVA Copolymer Mixture

  • Kim, Min Ji (Department of Chemical Engineering, Kongju National University) ;
  • Jeon, Jong-Ki (Department of Chemical Engineering, Kongju National University) ;
  • Park, Young-Kwon (Faculty of Environmental Engineering, University of Seoul) ;
  • Ko, Young Soo (Department of Chemical Engineering, Kongju National University) ;
  • Sohn, Jung Min (Department of Mineral Resources & Energy Engineering, Chonbuk National University)
  • 투고 : 2006.11.06
  • 심사 : 2006.12.08
  • 발행 : 2007.04.30
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

농업용 필름을 제조하는데 사용되는 EVA 공중합체, LDPE, LLDPE 혼합물의 접촉 열분해 반응에 있어서 MCM-41 촉매에 aluminium을 첨가가 생성물의 수율, 탄소 수 분포 등에 미치는 영향을 조사하였다. Aluminium은 direct 및 post 방법으로 첨가하였고, 열분해 반응은 액상 접촉과 기상 접촉 반응 결과를 비교하였다. Direct 또는 post 방법으로 aluminium이 첨가된 MCM-41에서 aluminium 첨가량이 증가할수록 Lewis 산점이 증가하여 전체 산점의 양이 증가하였는데 post 방법으로 제조된 촉매에서 산점의 양이 더 많이 증가하였다. 액상 접촉 반응에서 aluminium의 양이 증가하면 가벼운 탄화수소가 많이 생기는데, $C_5-C_{12}$ 범위의 탄소화합물의 생성에 Al-MCM-41-P 촉매가 더 효과가 컸다. 기상 접촉 반응에서는 Al-MCM-41-D와 Al-MCM-41-P사이의 차이가 액상 접촉 반응시보다 상대적으로 적게 나타났으나, 액상접촉 반응에 비해 $C_{13}-C_{32}$ 범위의 탄화수소가 크게 감소했음을 알 수 있다.

The effect of aluminium addition to MCM-41 on product yield and carbon number distribution was investigated in the catalytic cracking of a polymer mixture, LDPE, LLDPE, and EVA copolymer, with a composition similar to that found in real agricultural film wastes. Al-MCM-41 catalyst synthesized by post-synthetic grafting method (Al-MCM-41-P) as well as Al-MCM-41 catalyst synthesized by direct sol-gel (Al-MCM-41-D). The catalytic cracking of polymer mixture was carried out in vapor phase contact as well as in liquid phase contact. The amount of acid sites increased with aluminium addition by post method as well as direct method, which was seemed to be due to Lewis acid sites. In liquid phase catalytic cracking, the yield of light hydrocarbon fraction increased with aluminium addition. The effect of aluminium addition on production of $C_5-C_{12}$ hydrocarbons over Al-MCM-41-P catalysts was greater than that over Al-MCM-41-D catalysts. In the case of vapor phase catalytic cracking, the effect of aluminium addition was smaller than that of liquid phase catalytic cracking. The selectivity to $C_{13}-C_{32}$ hydrocarbons was smaller in vapor phase catalytic cracking.

키워드

과제정보

연구 과제 주관 기관 : 공주대학교

참고문헌

  1. Sharratt, P. N., Lin, Y. H., Garforth, A. A. and Dwyer, J., 'Investigation of the Catalytic Pyrolysis of High-Density Polyethylene over a HZSM-5 Catalyst in a Laboratory Fluidized-Bed Reactor,' Ind. Eng. Chem. Res., 36(12), 5118-5124(1997) https://doi.org/10.1021/ie970348b
  2. Kim, S. S. and Kim, S., 'Pyrolysis Characteristics of Polystyrene and Polypropylene in a Stirred Batch Reactor,' Chem. Eng. J., 98(1-2), 53-60(2003) https://doi.org/10.1016/j.cej.2003.10.005
  3. Faravelli, T., Pinciroli, M., Pisanol, F., Bozzano, G., Dente, M. and Ranzi, E., 'Thermal Degradation of Polystyrene,' J. Anal. Appl. Pyrolysis, 60(1), 103-121(2001) https://doi.org/10.1016/S0165-2370(00)00159-5
  4. Vitolo, S., Bresci, B., Seggiani, M. and Gallo, M. G., 'Catalytic Upgrading of Pyrolytic Oils over HZSM-5 Zeolite: Behaviour of the Catalyst When Used in Repeated Upgrading-regenerating Cycles,' Fuel, 80(1), 17-26(2001) https://doi.org/10.1016/S0016-2361(00)00063-6
  5. Dao, L. H., Haniff, M., Houle, A. and Lamothe, D., In: Soltes and T. A. Milne (Eds), Pyrolysis Oils from Biomass: Producing, Analyzing and Upgrading, ACS Symposium Series 376, Washington DC, 329-341(1998)
  6. Takuma, K., Uemichi, Y. and Ayame, A., 'Product Distribution From Catalytic Degradation of Polyethylene over H-gallosilicate,' Appl. Catal. A: General, 192(2), 273-280(2000) https://doi.org/10.1016/S0926-860X(99)00399-3
  7. Park, Y. K., Kim, J. S., Jeon, J. K., Lim, J. E., Kim, J. M. and Yoo, K. S., 'A Kinetic Study of Catalytic Degradation of Linear Low Density Polyethylene By MCM-41 Preparation Method,' Polymer(Korea), 29(2), 122-126(2005)
  8. Park, Y. K., MS Thesis, KAIST(1994)
  9. Park, H. J., Jeon, J. K., Yim, J. H., Dong, J. I., Yoo, K. S. and Park, Y. K., 'Catalytic Degradation of Polyethylene by Al-MCM-4,' J. Ind. Eng. Chem., in press (2007)
  10. Kim, J. M., Ko, C. H. and Ryoo, R., 'Catalytic Activities of Mesopores Molecular Sieve, MCM-41 : Hydrogenolysis and Partial Oxidation, ' Appl. Chem. Eng., 2(1), 1137-1140 (1996)
  11. Lee, S. H., Lee, D. K. and Park, S. G., 'Synthesis and Characterization of MCM-41 Type Aluminosilicates', 2003 Annual Summer Conference, The Korean Institute of Electrical and Electronic Material Engineers, 1231-1234(2003)
  12. Kim, J. H. and Niwa, M., 'Synthesis and Solid Acidic Property of MCM-41 Mesoporous Material,' J. Res. Inst. Catal., 18(1), 45-53 (2003)
  13. Chon, H. and Seo, G., Int. Catal., 4th ed., Hanrimwon Publishing Co., Seoul(2002)
  14. Song,, S. K., Wang, Y. and Ihm, S. K., 'Effect of Lanthanum Addition on the Thiophene Hydrodesulfurization Activity over Al-MCM-41 Supported Molybdenum Catalysts', Catal. Today, 111(3-4), 194-198(2006) https://doi.org/10.1016/j.cattod.2005.10.026
  15. Chakraborty, B. and Viswanathan, B., 'Surface Acidity of MCM-41 by in situ IR Studies of Pyridine Adsorption,' Catal. Today, 49(1-3), 253-260(1999) https://doi.org/10.1016/S0920-5861(98)00400-3