Abstract
The raw oriental lacquer produced in China was used in this study. This lacquer was diluted with ethanol and terpene in different solvent ratios. The diluted lacquer in the solvents had two layers. The upper layer was solvent soluble and the lower contained precipitates. Hanji was treated with the solvent solubles and the mixture containing precipitates, and then properties of the Hanji were evaluated. The average weight, thickness, and density of Hanji treated with oriental lacquer tended to gradually be decreased as the lower concentration of lacquer was used and as the solvent soluble was treated. Tensile strength of the treated Hanji decreased when the diluted lacquer was used and Hanji treated with terpene dilution at the ratio of lacquer to solvent of 1:5 (v/v) showed higher tensile strength than ones treated with ethanol dilution. The folding endurance decreased as the less concentrated lacquer was used and the highest value was obtained when 1:40 (v/v) of lacquer to solvent ratio in both ethanol and terpene mixture. Absorption ratio was higher in the Hanji treated with ethanol mixture, treated with the lacquer in lower concentration, and treated with ethanol mixture. Hanji treated with ethanol dilution at 1:20 (v/v) and the lower ratio of lacquer to solvent showed a hydrophobic property. Amount of the bound dye materials tended to be decreasing as the concentration of lacquer became lower and it was higher in Hanji treated with ethanol mixture than with terpene mixture.