Abstract
The freeze-thaw deterioration and chloride attack, which are the typical degradation factors for durability of marine concrete, are significantly affected by pore structures in terms of penetration and diffusion. These pore structures of concrete are closely related to the types and amount of AE agent, used to guarantee the resistance of freeze-thaw deterioration, and the elapsed time before concrete pouring. This paper evaluates the durability of concrete based on the results of tests on cylinder specimens and core specimens from mock-up members with different air content of 4~6% and 8~10%, respectively. According to the test results, the air content of hardened concrete is 2.5~5.2% at 7 days and 2.4~5.1% at 28 days. These air contents are about half of the initial values just after the concrete mixing. Judging from the amount of scale after the freeze-thaw test completed, air content of 8~10% is slightly more beneficial against the deterioration of concrete than air content of 4~6%. Meanwhile, the core specimens from mock-up members exhibit somewhat unfavorable freeze-thaw deterioration and chloride migration characteristic compared with the cylinder specimens tested in the laboratory under the same mixing condition, as to show 106% in freeze-thaw test and 160% in chloride diffusion coefficient test, respectively.
해양콘크리트의 대표적인 내구성 열화요인이라 할 수 있는 동결융해나 염해의 경우는 콘크리트내의 공극특성에 따라 침투 및 확산특성이 크게 상이하게 되는데, 이는 동결융해저항성 확보를 목적으로 사용되고 있는 AE제의 종류나 사용량 그리고 그의 경시변화 특성 등과 매우 밀접한 관계가 있다. 따라서 본 연구에서는 굳지않은 콘크리트의 목표 공기량을 각각 4~6%와 8~10%로 계획하여 실내시험을 실시한 후, 모의부재에서는 4~6%를 대상으로 평가하였다. 실험결과, 경화콘크리트의 공기량은 재령 7일에서 각각 2.5~5.2%, 재령 28일에서는 각각 2.4~5.1%정도로서 비빔직후 목표공기량의 절반수준인 것으로 나타났고, 동결융해 반복에 따른 스케일량은 목표공기량 8~10%의 경우가 4~6%에 비해 미미한 수준에서 다소 유리한 것으로 평가되었다. 한편, 모의부재에서 채취한 코어공시체의 동결융해 및 염화물 확산특성에서는 동일배합조건의 실내시험 결과에 비해 다소 불리한 것으로 나타났는데, 실내실험 결과에 비해 동결융해는 106%, 염화물 확산계수는 160% 수준인 것으로 나타났다.