Abstract
In this paper, the applicability of Hwangtoh, as an alternative of cement paste, is investigated for the solution of internal heat and shrinkage caused by the hydration of cement paste. Several small-sized specimens of Hwangtoh and ordinary portland concrete (OPC) were compared as to compressive strength, heat of hydration, and shrinkage strain. Moreover, the applicability to the construction structures was reviewed through the test of large-size specimens. The 28-day compressive strength of Hwangtoh concrete (HBC), ranged 18 to 33 MPa, can reach that of OPC. Not only the maximun internal temperature of HBC was read about 1/4 of OPC as it is cured, but also its shrinkage decreased more than the OPC did. Therefore, Hwangtoh binder is more favorable than cement binder in terms of its hydration heat and shrinkage under the construction of concrete.
본 연구는 비활성 황토결합재로 시멘트를 대체함으로써 시멘트의 수화 반응 등에 의한 콘크리트 내부 발열과 수축 특성을 연구하였다. 먼저 재료의 분석을 토대로 압축강도, 슬럼프, 공기량을 살펴보았다. 소형시편과 대형시편을 제작하였고, 보통콘크리트 (OPC)와 황토콘크리트 (HBC)의 수화열, 수축을 측정하여 비교 평가하였다. 황토결합재는 압축강도가 $18{\sim}33\;MPa$로 보통강도 콘크리트의 강도를 발현하였고, 유동성도 확보되는 결과를 보였다. 소형시편에서는 HPC는 OPC에 비해 양생시 내부의 최고온도가 약 1/4 정도로 낮게 나타나고 수축 역시 HBC는 OPC에 비하여 감소하였다. 대형시편에서도 HBC는 OPC에 비해 내부온도가 낮게 나타났으며 수축 역시 60일 기점으로 OPC의 상대적으로 매우 낮은 수축률을 보였다. 따라서 비활성 황토 결합재는 일정강도와 유동성을 확보할 수 있는 재료이며 친환경적 재료이다. 수화열과 수축에 있어 내구성능을 확보하는데 긍정적으로 사료된다.