Crystallization of the Titania Coated on Kaolinite Powder using Sol-Gel Method

졸-겔법에 의해 카올리나이트 분말에 코팅된 티타니아의 결정화

  • Yang, Young-Cheol (Minerals and Materials Processing Division, Korea Institute of Geoscience & Mineral Resources) ;
  • Jeong, Soo-Bok (Minerals and Materials Processing Division, Korea Institute of Geoscience & Mineral Resources) ;
  • Kim, Byoung-Gyu (Minerals and Materials Processing Division, Korea Institute of Geoscience & Mineral Resources)
  • 양영철 (한국지질자원연구원 자원활용소재연구부) ;
  • 정수복 (한국지질자원연구원 자원활용소재연구부) ;
  • 김병규 (한국지질자원연구원 자원활용소재연구부)
  • Published : 2008.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

$TiO_2$ coatings on kaolinite powders by sol-gel method were carried out using mixture of titanium isopropoxide, ethanol as solvent, HCl as a catalyst and $H_{2}O$ for hydrolysis. The mole ratio of reaction mixture, stirring time. aging time, crystallization time and crystallization temperature influenced to the crystallization of $TiO_2$ coated on kaolinite and metakaolinite Powders. Optimum condition for $TiO_2$ coatings on kaolinite was as follows; TIP 0.1 mol, $H_{2}O$ 0.15 mol, HCl 0.005 mol, ethanol 100 ml, raw kaolinite 50 g, stirring time 4 hrs, aging time 24 hrs, crystallization time 2 hrs and crystallization temperature $1050^{\circ}C$. The crystallinity of the anatase under optimum condition was about 17.61%. The anatase crystallinity of the $TiO_2$ coated on raw kaolinitc powders (17.61% at $1050^{\circ}C$) was higher at the lower calcination temperature compared with metakaolinite (17.39% at $1200^{\circ}C$).

카올리나이트(kaolinite) 분말의 티타니아(Titania, $TiO_2$) 포팅을 위한 출발물질로서 인도네시아산 카올리나이트와 티타늄-아이소프로폭사이드(titanium isopropoxidc, TIP)가 사용되었으며, 실험은 졸-겔법(sol-gel method)으로 수행되었다. 또한 강매로서 에탄올이, 가수분해 반응을 위해 물이 사용되었으며 촉매로서 염산을 첨가하였다. 카올리나이트 분말의 소성여부에 따른 영향을 검토하기 위해 카올리나이트와 메타카올리나이트(metakaolinite)를 대상으로 각각 실험하였으며, 반응 혼합물의 몰비, 교반시간, 숙성시간, 결정화 시간과 온도의 변화에 따른 티타니아 결정도를 검토하였다. 실험조건 TIP 0.1 몰(mol), 물 0.15 몰, 염산 0.005 몰, 에탄을 100 ml, 카올리나이트 50 g, 교반 4시간, 숙성 24시간, 결정화온도 $1050^{\circ}C$, 결정화 2시간에서 가장 높은 아나타제 결정도 17.61%를 나타냈다. 결정화온도의 변화에 따른 아나타제 결정도 분석결과, 카올리나이트와 메타카올리나이트 분말에 코팅된 티타니아는 $1050^{\circ}C$와 $1200^{\circ}C$에서 각각 37.61%, 17.39%로 최고의 결정도가 관찰되었다. 즉, 카올리나이트 분말에 코팅된 티타니아가 메타카올리나이트에 비해 더 낮은 온도에서 더 높은 결정도를 나타냈다.

Keywords

References

  1. 이종근 (1990) 무기재료 원료공학, 반도출판사, 서울, 42p
  2. Brinker, C.J. and Scherer, G.W. (1990) SOL-GEL SCIENCE, Academic Press, Inc
  3. Cullity, B.D. (1977) Elements of X-ray Diffraction, Department of Metallurgical Engineering and Materials Science University of Notre Dame, 508-521
  4. Kominami, H., Masaaki, K., Takada, Y., Inoue, M., Inui, T., and Kera, Y. (1999) Hydrolysis of Titanium Alkoxide in Organic Solvent at High Temperatures : A New Synthetic Method for Nanosized, Thermally Stable Titaium(IV) Oxide, Ind. Eng. Chem. Res., 38, 3925-3931 https://doi.org/10.1021/ie9901170
  5. Kumar, P., Keizer, K., Burggraaf, A.J., Okubo, T., Nagamoto, H., and Morooka, S. (1992) Densification of Nanostructured Titania Assisted by a Phase Transformation, NATURE, 358, 48-51 https://doi.org/10.1038/358048a0
  6. Mizuno, T., Phalippou, J., and Zaraulei, J. (1985) Evolution of the Viscosity Containing Metal Alkoxide, Glass Technology, 26, 1
  7. Ovenstone, J. and Yanagisawa, K. (1999) Effect of Hydrothermal Treatment of Amorphous Titania on the Phase Change from Anatase to Rutile during Calcinaton, Chem. Mater., 11, 2770-2774 https://doi.org/10.1021/cm990172z
  8. Ragai, J. (1985) Aging Studies on Some Titania Gels, J. Chem. Tech. Biotechnol., 35A, 263-269
  9. Retuert, J. and Quijada, R. (2000) Titania Coating on High and Low Surface Area Spherical Silica Particles by a Sol-Gel Method, J. Mater. Chem., 10, 2818 https://doi.org/10.1039/b005406m
  10. Sakka, S. and Kamiya, K. (1984) Preparation of Shaped Glasses Through the Sol-Gel Method, Mat. Sci. Res., 17, 83-94
  11. Schrijnemakers, K., Impens, N.R.E.N., and Vansant, E.F. (1999) Deposition of Titania Coating on Silica by Means of the Chemical Surface Coating, Langmuir, 15, 5807-5808 https://doi.org/10.1021/la9812469
  12. Selvarah, U., Prasadarao, A., Komarneni, S., and Roy, R. (1992) Sol-Gel Fabrication of Epitaxial and Oriented $TiO_2$ Thin Films, J. Am. Ceram. Soc., 75, 1167-1170 https://doi.org/10.1111/j.1151-2916.1992.tb05554.x
  13. Sugimoto, T., Okada, K., and Itoh, H. (1997) Synthesis of Uniform Spindle-Type Titania Particles by the Gel-Sol Method, J. Colloid Interface Sci., 193, 140 https://doi.org/10.1006/jcis.1997.5037
  14. Wang, C.C. and Ying, J.Y. (1999) Sol-Gel Synthesis and Hydrothermal Procesing of Anatase and Rutile Titania Nanocrystals, Chem. Mater., 11, 3113-3120 https://doi.org/10.1021/cm990180f
  15. Yi, G. and Sayer, M. (1991) Sol-Gel Processing of Complex Oxide Films, CERAMIC BULLETIN, 70, 1173
  16. Yoko, T., Kamiya, K., and Sakka, S. (1987) Photoelectrochemical Properties of $TiO_2$ Films Prepared by the Sol-Gel Method, Yogyo-Kyokai-Shi., 95, 12
  17. Zhang, J.Y. and Boyd, I.W. (2000) Titanium Dioxide Films Prepared by Photo-induced Sol-Gel Procesing Using 172nm Excimer Lamps, Surface and Coatings Technology, 125, 424 https://doi.org/10.1016/S0257-8972(99)00617-9
  18. Zhu, Y.F., Zhang, L., Yao, W.Q., and Cao, L.L. (2000) The Chemical States and Properties of Doped $TiO_2$ Film Photocatalyst Prepared using the Sol-Gel Method with TiCl4 as a Precursor, Applied Surface Science, 158, 32-37 https://doi.org/10.1016/S0169-4332(99)00587-5