Characteristics of Electroconductive Paper Manufactured with Carbon Fiber

탄소섬유를 이용한 전도성 종이의 제조 및 특성

  • Kim, Bong-Yong (Department of Wood Science and Technology, Kyungpook National University)
  • 김봉용 (경북대학교 임산공학과)
  • Published : 2009.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

Electroconductive papers were manufactured as handsheet by mixing carbon fiber in LBKP and BCTMP. The electrical conductivity of the paper was improved by increasing carbon fiber content and basis weight. The porosity was increased and tensile strength was decreased by the addition of carbon fiber. Electrical conductivity of carbon fiber and BCTMP-based sheet was much better than those of carbon fiber and LBKP-based one. This result indicated that the electrical conductivity of paper can be affected by the kinds of raw material of wood fibers used.

Keywords

References

  1. 정준, 유승곤, 탄소섬유 강화종이의 전기전도도와 표면 온도, 화학공학 42(5):598-604(2004)
  2. Cho, J. W and Choi, J. S., Relationship Between Electrical Resistance and Strain of Carbon Fibers upon Loading, J. Appl. Polym. Sci.,77(9) : 2082-2087 (2000) https://doi.org/10.1002/1097-4628(20000829)77:9<2082::AID-APP26>3.0.CO;2-W
  3. Zhang, C., Yi, X. S., Yui, H., Asai, S. and Sumita, M., Morphology and Electrical Properties of Short Carbon Fiber-Filled Polymer Blends : High-Density Polyethylene Polymethyl Methacrylate, J. Appl. Polym. Sci., 69(9) : 1813-1819(1998) https://doi.org/10.1002/(SICI)1097-4628(19980829)69:9<1813::AID-APP16>3.0.CO;2-M
  4. Lozano, K., Bonilla-Rios, J. and Baeera, E. V., A Study on Nonfiber-Reinforced Thermoplastic Composites( ) : Investigation of the Mixing Rheology and Conduction Properties, J. Appl. Polym. Sci., 80(8) : 1162-1172(2001) https://doi.org/10.1002/app.1200
  5. Krekel, G., Huttinger, K. J. and Hoffman, W .P., The Relevance of the Surface-Structure and Surface- Chemistry of Carbon-Fibers in Their Adhesion to High Temperature Thermoplastics, J. Mater. Sci., 29(13) : 3461-3468(1994) https://doi.org/10.1007/BF00352050