Characteristics of Uncofined Compressive Strength and Flow in Controlled Low Strength Materials Made with Coal Ash

석탄회를 활용한 저강도고유동화재의 일축압축강도 및 플로우 특성

  • 공진영 (한양대학교 대학원 건설환경공학과) ;
  • 강형남 (한양대학교 대학원 건설환경공학과) ;
  • 천병식 (한양대학교 건설환경공학과)
  • Published : 2010.01.31
Download PDF
⟨ Previous Next ⟩

Abstract

Controlled low strength material (CLSM) is a flowable mixture and does not need to be compacted. It is produced by mixing portland cement, fly ash, fine aggregates, water and chemical admixtures. Sand is the most commonly used fine aggregates in the conventional CLSM, but it is getting more and more difficult to obtain sand in Korea. In this study, the characteristics of unconfined compressive strength, flow and applicability of a new CLSM that is produced by mixing of pond ash, fly ash, water, cement are examined. An unconfined compressive strength satisfies the standard unconfined compressive strength (0.5~1.0 MPa) were obtained when the mixture ratio of pond ash and fly ash is 30:70~70:30, cement ratio is 3.0~5.0%, and water content is 31~34%. The results of flow test indicate that the mixture ratio of pond ash and fly ash which satisfy the standard How value (0.2 m) is 30:70~70:30.

저강도고유동화재는 다짐이 필요 없고 유동성이 큰 물질로 일반적으로 시멘트, 비회, 잔골재, 물, 혼화제 등을 혼합하여 만들어진다. 기존의 CLSM은 잔골재로 모래를 사용하고 있으나 때문에 모래가 점점 구하기 어려워지는 현재 우리나라 실정에서는 그대로 사용하기 곤란하다. 본 연구에서는 모래대신 매립회를 이용하여 매립회, 비회, 시멘트, 물의 혼합물로 만들어진 CLSM의 강도특성을 조사하여 사용가능성을 제시하고자 한다. 일축압축강도실험결과 기준 일축압축강도(0.5MPa~1.0MPa)를 만족하는 배합비는 매립회와 비회의 혼합비 0:100~70:30, 시멘트비 3.0~5.0%, 함수비 31~34%로 나타났다. 플로우시험 결과 매립회와 비회를 혼합하여 사용하는 모든 경우(매립회와 비회의 비 30:70~70:30)에서 기준 플로우값(0.2m)를 만족하였다.

Keywords

References

  1. 박재헌, 이관호, 조재윤, 김석남 (2004), "현장발생토 CLSM을 이용한 지하매설관의 변형", 한국지반공학회논문집, 제20권 3호, pp.129-139.
  2. 조재윤, 이관호, 이인모 (2000), "유동특성을 이용한 폐주물사 혼합물의 옹벽뒷채움재 연구", 한국지반공학회논문집, 제16권 4호, pp.17-30.
  3. 원종필, 이용수 (2001), "Bottom Ash를 흔합한 저강도 고유동 충전재의 특성", 콘크리트학회논문집,13권 3호, pp.294-300.
  4. 이관호, 송창섭 (2006), "현장발생토사 재활용 유동성채움재를 이용한 지하매설관의 거통평가", 한국도로학회 논문집, 제18권 2호, pp.1-12.
  5. 이관호, 김주득, 현성철, 송용선, 이병식 (2007), "해양준설토를 CLSM을 이용한 지하매설관 변형특성", 한국방재학회논문집, 제7권 5호, pp.129-137.
  6. 임유진, 서창범 (2009), "화강풍화토를 이용한 CLSM의 공학적 특성평가", 한국방재학회논문집, 제9권 3호, pp.19-26.
  7. 환경부 (2008), "제4차자원재활용기본계획", 환경부, pp.100-102
  8. ACI Committee 229 (1994), "Controlled Low Sπength Materials (CLSM)", American Concrete Institute, 229R-2. pp.1-12.
  9. Amster K. Howard, Jennifer L. Hitch (1998), "The design and application of controlled low-strength materials (flowable fill), ASTM intemational", pp.156-162.
  10. Amon, J. A., Controlled Low-Strength Material, The Construction Specifier, December 1990, pp.98-101.
  11. ASTM (2002), "Standard Test Method for Preparation and Testing of Controlled Low Strength Material (CLSM) Test Cylinders", ASTM D 4832, American Society for Testing Materials.
  12. ASTM (2004), "Standard Test Method for Flow Consistency of Controlled Low Strength Material (CLSM)", ASTM D 6103, American Society for Testing Materials.
  13. NRMCA (1995), "Guide Specification for Controlled Low Strength Materials (CLSM)", National Readymixed Concrete Association, pp.5-7.
  14. Sumio Horiuchi (1996), "石炭灰の水域埋立てへの利用に關する研究", 堀内澄夫 pp.97-131.
  15. Tarun R. Naik, Rudolph N. Kraus (2002), "Properties of Flowablc Slurry Containing Wood Ash", Report No. CBU-2002-14, pp.5-9.
  16. Tarun R. Naik, Rudolph N. Kraus (2004), "Properties of Flowable Selt:Compacting Slurry Using Quarry By-Products and Ponded CCPs", Publication SP, v.22l, pp.523-538.
  17. TRB (2008), "Development of a Recommended Practice for Use of Controlled Low-Strength Material in Highway Construction", NCHRP Report 597, U.S. Transportation Research Board, pp.3-59.