Abstract

Recently, many researches on bottom ash which is produced in the burning process of power plant are actively performed for its utilization for soil-subbase materials. In this paper, bottom ashes from 5 different power plants are prepared and several tests including compaction, CBR, and tri-axial compression are carried out for mixed bottom ash and weathered soil considering 3 replacement ratio of 30%, 50%, and 70%. Through the tests, CBR result over 20 are evaluated without plastic property, which shows availability of subbase material. With higher increase in replacement ratio of bottom ash, CBR of mixed soil increases due to the higher mechanical performance of bottom ash. However, replacement effects of bottom ash on friction angle and cohesion are evaluated to be little since bottom ash plays a little role in rearrangement of mixed soil. Bottom ash with a good mechanical property is evaluated to have reasonable bearing capacity which shows a good property for subbase materials.

최근 들어 산업부산물인 저회를 지반 매립재로 활용하려는 연구가 활발하게 진행되고 있다. 본 연구에서는 국내 5개 사에서 채취된 저회와 풍화토 혼합하여, 3가지 저회의 혼합비 (30%, 50%, 70%)에 따른 다짐실험, CBR 실험 및 삼축 압축실험 등이 수행되었다. 실험 결과, 저회를 혼입한 혼합토의 CBR값은 20을 상회하였으며, 소성을 보이지 않아 성토재료로 사용이 가능할 것으로 평가되었다. 혼합토에 사용된 저회의 역학적 성능이 풍화토보다 우수하므로, 혼합비가 증가할수록 혼합토의 CBR값은 뚜렷한 증가를 나타내었다. 그러나, 배합후 입자배열에는 큰 영향을 주지 못하므로, 혼합비에 따른 내부마찰각 및 점착력의 변화는 뚜렷하게 평가되지 못했다. 저회는 시료 자체의 강성이 있으므로, 지지력이 풍화토에 비하여 크게 평가되었으며, 성토재료로서의 활용할 수 있음을 실험적으로 규명하였다.

Keywords

• Bottom ash;
• Subbase material;
• CBR (California Bearing Ratio);
• Tri-axial compression test;
• Cohesion

• 저회;
• 성토재료;
• 삼축압축실험;
• 점착력;