Removal of Impurities from Metallurigical Grade Silicon by Acid Washing

금속급(金屬級) 실리콘에서 산세척(酸洗滌)에 의한 불순물(不純物)의 제거(除去)

  • Lee, Man-Seung (Department of Advanced Materials Science & Engineering, Mokpo National University) ;
  • Kim, Dong-Ho (Innovation Silicon Co Ltd.)
  • 이만승 (목포대학교 공과대학 신소재공학과) ;
  • 김동호 (이노베이션 실리콘)
  • Received : 2011.01.14
  • Accepted : 2011.02.10
  • Published : 2011.02.26

Abstract

Impurity removal from metallurgical grade silicon by acid washing at $50^{\circ}C$ was investigated by employing sulfuric, nitric acid and the mixture of hydrochloric and hydrofluoric acid. Acid washing treatment had no effect on the removal of boron and the concentration of this clement after treatment was rather increased. In our experimental range, the removal percentage of phosphorus was 60%. In the acid washing with sulfuric and nitric acid, the removal percentage of major impurities was below 50%, which indicates that refining effect was not great with these acids. Acid washing with the mixture of hydrochloric and hydrofluoric acid led to removal percentage of higher than 90%. Data on the purity of silicon after acid washing at various conditions are reported.

산세척을 통해 금속급 실리콘을 정련하기 위해 황산, 질산, 염산과 불산의 혼산 용액을 사용하여 $50^{\circ}C$에서 불순물의 제거 거동을 조사하였다. 금속급 실리콘에 함유된 불순물중 붕소는 산세척으로 제거되지 않았고, 농축효과로 인해 처리 후 농도가 종가하였다. 본 실험범위에서 인은 약 60% 정도 제거되었다. 황산과 질산용액으로 처리시 주요 불순 금속의 제거율은 50% 미만으로 정련 효과가 크지 않았다. 염산과 불산의 혼산으로 산세척하면 주요 불순 금속이 90% 정도 제거되었다. 각 산세척조건에서 얻은 실리콘의 순도와 주요 불순 금속들의 제거율에 대한 자료를 제시하였다.

Keywords

References

  1. 김희영, 2008: 태양전지용 실리콘소재의 기술개발 동향, 전기전자재료, 21(11), pp. 3-11.
  2. 신제식, 김대석, 김기영, 손인진, 문병문, 2009: 태양전지 원재료로 사용하기 위한 폴리실리콘 미세분말의 무점결제 성형, 자원리싸이클링, 18(1), pp. 38-43.
  3. Santos, I.C., Gonalves, A.P., Santos, C.S., Almeida, M., Afonso, M.H. and Cruz, M.J., 1990: Purification of metallurgical grade silicon by acid leaching, Hydrometallurgy, 23, pp. 237-246. https://doi.org/10.1016/0304-386X(90)90007-O
  4. Habashi, F., 1997 : Handbook of extractive metallurgy Vol 4, Wiley-VCH, NY., p. 1863.
  5. Ciftja, A., Zhang, L., Engh, T.A. and Kvithyld, A., 2006: Purification of solar cell materials through filtration, Rare metals, 25, pp. 180-185. https://doi.org/10.1016/S1001-0521(07)60070-9
  6. Yuge, N., Baba, H, Sakaguhi, Y., Nishikawa, K., Terashima, H. and Aratani, F., 1994: Purification of metallurgical silicon up to solar grade, Solar Energy Materials and Solar Cells, 34, pp. 243-250. https://doi.org/10.1016/0927-0248(94)90046-9
  7. Margarido, F., Bastos, M.H., Figueiredo, M.O. and Martins, J.P., 1994: The structural effect on the kinetics of acid leaching refining of Fe-Si alloys, Materials Chemistry and Physics, 38, pp. 342-347. https://doi.org/10.1016/0254-0584(94)90211-9
  8. Margarido, F., Martins, J.P., Figueiredo, M.O. and Bastos, M.H., 1993: Kinetics of acid leaching refining of an industrial Fe-Si, Hydrometallurgy, 34, pp. 1-11. https://doi.org/10.1016/0304-386X(93)90077-Q
  9. Margarido, F., Martins, J.P., Figueiredo, M.O. and Bastos, M.H., 1993: Refining of Fe-Si alloys by acid leaching, Hydrometallurgy, 32, pp. 1-8. https://doi.org/10.1016/0304-386X(93)90052-F
  10. Juneja, J.M. and Mukherjee, T.K., 1986: A study of the purification of metallurgical grade silicon, Hydrometallurgy, 16, pp. 69-75. https://doi.org/10.1016/0304-386X(86)90052-6
  11. 정혜영, 김영운, 유학도, 이상학, 1999: 실리콘 웨이퍼중의 금속 불순물 분석을 위항 전처리, 대한화학회지, 43(4), pp. 412-417.

Cited by

  1. Experimental investigations for recycling of silicon and glass from waste photovoltaic modules vol.47, 2012, https://doi.org/10.1016/j.renene.2012.04.030
  2. 금속급(金屬級) 실리콘에서 슬래그 처리(處理)에 의한 붕소(硼素)의 제거(除去) vol.20, pp.3, 2011, https://doi.org/10.7844/kirr.2011.20.3.055
  3. 칼슘 첨가(添加)-용융(溶融) 금속급(金屬級) 실리콘의 왕수(王水) 침출(浸出)에 의한 철(鐵)과 인(憐)의 제거(除去) vol.20, pp.5, 2011, https://doi.org/10.7844/kirr.2011.20.5.034
  4. 순도가 향상된 금속급 실리콘 제조를 위한 산침출 연구 vol.18, pp.11, 2017, https://doi.org/10.5762/kais.2017.18.11.118
  5. 습식 화학 공정에 의한 태양전지로부터 고순도 실리콘 회수 및 이를 이용한 태양전지 재제조 vol.29, pp.11, 2011, https://doi.org/10.3740/mrsk.2019.29.11.697